Assessing the bond strength of short fiber composites to dentin using various air abrasion particles.

Purpose: This study investigated the bond strength between short fiber-reinforced resin composite (SFC) and dentin following air abrasion with various types of abrasive particles.

Methods: A total of 120 human molars were prepared for a shear bond strength (SBS) test of the resin composite. The teeth were divided into 12 groups (n = 10/group) based on the air abrasion particle used.

Impact of restorative material on fracture behaviors of class II restoration in endodontically treated deciduous molars.

The purpose of this study was to investigate the fracture behavior of endodontically treated (ET) deciduous molar when directly restored with different restorative materials in Class II (MO) cavities in comparison with permanent teeth. MO cavities were prepared with 2.4-2.

Effect of different surface treatments on shear bond strength of autopolymerizing repair resin to denture base materials processed with different technologies.

Purpose: To evaluate the effect of chemical, mechanical, and combination surface treatments on the shear bond strength (SBS) of autopolymerizing repair resin to conventional heat-cured, computer aided design (CAD)-computer aided manufacturing (CAM) milled, and three-dimensionally (3D) printed denture base materials.

Methods: Specimens were fabricated and divided according to the surface treatment as follows: no surface treatment (control group), monomer treatment (monomer group), resin remover treatment (resin remover group), roughening with 180 FEPA grit abrasive paper followed by monomer treatment (180-grit plus monomer group), and air particle abrasion (air abrasion group). Autopolymerizing resin cylinders were attached before accelerated aging of the specimens in water at 100 °C for 16 h.

Bioactive glasses promote rapid pre-osteoblastic cell migration in contrast to hydroxyapatite, while carbonated apatite shows migration inhibiting properties.

Different biomaterials have been clinically used as bone filling materials, although the mechanisms behind the biological effects are incompletely understood. To address this, we compared the effects of five different biomaterials: two bioactive glasses (45S5 and S53P4), hydroxyapatite (HAP), carbonated apatite (CAP), and alumina on the in vitro migration and viability of pre-osteoblastic cells. In addition, we studied the effects of biomaterials' calcium release on cell migration, viability and differentiation.

Zirconia implants interfere with the evaluation of peri-implant bone defects in cone beam computed tomography (CBCT) images even with artifact reduction, a pilot study.

Objectives: Three-dimensional cone beam computed tomography (CBCT) imaging can be considered, especially in patients with complicated peri-implantitis (PI). Artifacts induced by dense materials are the drawback of CBCT imaging and the peri-implant bone condition may not be assessed reliably because the artifacts are present in the same area. This pilot study investigates the performance of the artifact reduction algorithm (ARA) of the Planmeca Viso G7 CBCT device (Planmeca, Helsinki, Finland) with three different implant materials and imaging parameters.

Retrospective Analysis of Artifacts in Cone Beam Computed Tomography Images Used to Diagnose Chronic Rhinosinusitis.

Background: Cone beam computed tomography (CBCT) is frequently used to corroborate the signs and symptoms of chronic rhinosinusitis (CRS). However, artifacts induced by dental restorations might complicate the diagnosis of CRS. Here, we assessed the frequency and location of artifacts in CBCT images taken to confirm the CRS.

Effect of bioactive glass particles on mechanical and adhesion properties of resin cements.

Purpose: The aim of this study is to evaluate the mechanical and adhesive properties of three different resin cements with bioactive glass (BAG) incorporated in two different ratios.

Methods: BAG was added to different resin cements (3M Rely-X Ultimate, GC Link Ace, and GC Link Force) in different ratios (5% and 10% by weight). The three-point flexural strength, microhardness, and bond strength properties were evaluated.

Load-bearing composite fracture-fixation devices with tailored fibre placement for toy-breed dogs.

Fibre reinforced composites are attractive materials for hard tissue reconstructions, due to the high strength and low flexural modulus. However, lack of contourability in the operation theatre inhibits their clinical applications. The study presents a novel in situ contourable composite implant system for load-bearing conditions.

Two-body wear and surface hardness of occlusal splint materials.

The aim of this in vitro study was to evaluate the wear and surface hardness of nine materials for conventional manufacturing, subtractive milling, and 3D printing of occlusal splints, as well as to evaluate the differences in wear and surface hardness between rigid and flexible 3D-printed occlusal splint materials. Two-body wear and Vickers hardness tests were performed. The vertical wear depth and Vickers hardness values were statistically analyzed.

Mechanical Properties Evaluation of Three Different Materials for Implant Supported Overdenture: An In-Vitro Study.

Aim: the aim of this study was to compare the flexural strength and elastic modulus of three-dimensionally (3D) printed, conventional heat-cured, and high-impact implant-supported overdenture materials specimens. Materials and Methods: Thirty implant-supported overdenture materials specimens (bar-shaped, 65.0 × 10.

Physicochemical and biological characterization of silica-coated alumina particles.

Objectives: A tribochemical silica-coating (TSC) method has been developed to improve the adhesion of dental resin composites to various substrates. The method utilizes airborne-particle abrasion using particles having a silica surface and an alumina core. The impact of the TSC method has been extensively studied but less attention has been paid to the characterization of the silica-modified alumina particles.

Fracture behavior of discontinuous fiber-reinforced composite inlay-retained fixed partial denture before and after fatigue aging.

Purpose: To evaluate the fracture behavior of inlay-retained fixed partial dentures (IRFPDs) made of experimental short fiber-reinforced composite (SFRC) computer-aided design/computer-aided manufacturing (CAD/CAM) block before and after cyclic fatigue aging.

Methods: Five groups (n=20/group) of three-unit posterior IRFPDs were fabricated. The first and second groups were CAD/CAM fabricated from experimental SFRC blocks or lithium-disilicate (IPS e.

The biomechanical effect of root amputation and degree of furcation involvement on intracoronally splinted upper molar teeth - An in vitro study.

Objectives: The aim of this study was to evaluate the effect of the amount of periodontal support and the presence or absence of root amputation on the fracture resistance of intracoronally splinted maxillary molar teeth.

Materials And Methods: 48 extracted human upper first molars and 48 s premolars were included in the study. All teeth underwent standard mesio-occluso-distal (MOD) (molars) and standard occluso-distal (OD) (premolars) cavity preparation.

Effect of specific retention biomaterials for ball attachment on the biomechanical response of single implant-supported overdenture: A finite element analysis.

Purpose: The purpose of this finite element analysis (FEA) was to evaluate the effect of specific retention biomaterials with different elastic modulus on the biomechanical response to the axial and off-axial biting loads of a mandibular midline single implant-supported overdenture (SIO) model.

Methods: Five 3-dimensional (3D) finite element models of an edentulous mandible with SIO were designed as follows: model M with a titanium retentive element for ball attachment, model P with a PEEK retentive element, model S with a silicone resilient liner retentive element, model T with a thermoplastic acrylic resin retentive element made from a CAD-CAM material, and model A with a polyacetal resin retentive element. Posterior bilateral vertical load (PV) at the 1st molar areas and anterior oblique load (AO) at the incisal edge of the mandibular central incisors at a 30-degree angle of 100 N were applied.

Structural and elemental characterization of glass and ceramic particles for bone surgery.

Objective: Clinically used bioceramics have been characterized previously with different kinds of methods and comparison of results have proven to be difficult due to varieties of the material properties of interest. Therefore, in this study we compared clinically commonly used bioceramics of hydroxyapatite and carbonate apatite, two bioactive glasses 45S5 and S53P4, and alumina with respect of properties which according to the present knowledge are significant for bone biology.

Methods: Physicochemical properties of the materials were characterized by various methods.

A Polymer for Application as a Matrix Phase in a Concept of In Situ Curable Bioresorbable Bioactive Load-Bearing Continuous Fiber Reinforced Composite Fracture Fixation Plates.

The use of bioresorbable fracture fixation plates made of aliphatic polyesters have good potential due to good biocompatibility, reduced risk of stress-shielding, and eliminated need for plate removal. However, polyesters are ductile, and their handling properties are limited. We suggested an alternative, PLAMA (PolyLActide functionalized with diMethAcrylate), for the use as the matrix phase for the novel concept of the in situ curable bioresorbable load-bearing composite plate to reduce the limitations of conventional polyesters.

The Viability and Growth of HaCaT Cells After Exposure to Bioactive Glass S53P4-Containing Cell Culture Media.

Hypothesis: Bioactive glass (BG) S53P4 reduces the viability of epidermal keratinocyte-derived immortalized cell line, HaCaT in sufficient concentrations in vitro.

Background: Although used in mastoid obliteration surgery, there is no data available on whether BG S53P4 granules have an inhibitory or excitatory effect on keratinocytes, found in normal skin and ear cholesteatoma in vivo.

Methods: HaCaT cell cultures were incubated with a direct BG S53P4 granule contact.

Behaviour of different bioactive glasses incorporated in polydimethylsiloxane endodontic sealer.

Objectives: The aim of this study was to analyze the behavior of different bioactive glass fillers (BAGs) embedded in a polydimethylsiloxane matrix of an endodontic sealer.

Methods: Three different endodontic sealers were fabricated using S53P4, 45S5 and 18-06 glass fillers. Endodontic sealer Guttaflow Bioseal consisting of polydimethylsiloxane (PDMS) matrix was used as base of the experimental sealers.

The effect of chlorhexidine and dimethyl sulfoxide on long-term sealing ability of two calcium silicate cements in root canal.

Objectives: To evaluate the long-term effect of chlorhexidine (CHX) and dimethyl sulfoxide (DMSO) on the sealing ability and biomineralization of two different calcium silicate cements (CSC) in root canal.

Methods: Sixty human third molar root canals were obturated with ProRoot MTA or Biodentine. Before obturation the canals were irrigated with saline (control), 2% CHX or 5% DMSO.

Evaluation of the mechanical properties and degree of conversion of 3D printed splint material.

Objective: To evaluate the effect of post-curing method, printing layer thickness, and water storage on the mechanical properties and degree of conversion of a light-curing methacrylate based resin material (IMPRIMO® LC Splint), used for the fabrication of 3D printed occlusal splints and surgical guides.

Methods: 96 bar-shaped specimens were 3D printed (Asiga MAX), half of them with a layer thickness of 100 μm (Group A), and half with 50 μm (Group B). Each group was divided in three subgroups based on the post-curing method used: post-curing with light emitting diode (LED) and nitrogen gas; post-curing with only LED; and non-post-curing.