Statement Of Problem: Because water sorption of autopolymerizing acrylic reline resins is accompanied by volumetric change, it is a physical property of importance. As residual monomer leaches into the oral fluids and causes tissue irritation, low solubility of these resins is desired. Another requirement is a satisfactory bond between the autopolymerizing acrylic resins and the denture base acrylic resin.
Purpose: This study compared the water sorption, solubility, and the transverse bond strength of 2 autopolymerizing acrylic resins (Duraliner II and Kooliner) and 1 heat-polymerizing acrylic resin (Lucitone 550).
Material And Methods: The water sorption and solubility test was performed as per International Standards Organization Specification No. 1567 for denture base polymers. Bond strengths between the autopolymerizing acrylic resins and the heat-polymerizing acrylic resin were determine with a 3-point loading test made on specimens immersed in distilled water at 37 degrees C for 50 hours and for 30 days. Visual inspection determined whether failures were adhesive or cohesive.
Results: Duraliner II acrylic resin showed significantly lower water sorption than Kooliner and Lucitone 550 acrylic resins. No difference was noted in the solubility of all materials. Kooliner acrylic resin demonstrated significantly lower transverse bond strength to denture base acrylic resin and failed adhesively. The failures seen with Duraliner II acrylic resin were primarily cohesive in nature.
Conclusions: Autopolymerizing acrylic reline resins met water sorption and solubility requirements. However, Kooliner acrylic resin demonstrated significantly lower bond strength to denture base acrylic resin.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1016/s0022-3913(98)70008-3 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Clinical outcomes of conversion prosthesis in immediately loaded implants: A retrospective study.
J Prosthodont
January 2025
Department of Community Medicine and Health Care, University of Connecticut Health Center, Farmington, Connecticut, USA.
Purpose: The primary objective of this retrospective study was to evaluate the survival outcomes of immediately loaded acrylic resin complete arch fixed implant-supported prosthesis (CAFIP) fabricated from the denture conversion protocol. The secondary objective was to evaluate the early implant survival outcomes associated with these prostheses.
Material And Methods: A retrospective chart review was conducted to study the clinical outcomes data of immediately loaded conversion prostheses and immediately loaded implants.
Next-Generation Dental Materials: Exploring Bacterial Biofilm Formation on 3D-Printable Resin-Based Composites.
J Funct Biomater
January 2025
Dental Research Division, Guarulhos University, Guarulhos 07023-070, SP, Brazil.
This study evaluated the microbial growth profile of subgingival multispecies biofilm on 3D-printable resin-based composites (PRBCs). A 96-well cell plate cultivated a 39-species biofilm associated with periodontitis over 7 days. Cylindrical specimens with 12 mm high and 3 mm diameters were prepared by the PRBC group (Cosmos Temp-Yller; Prizma 3D Bio Crown; Prizma 3D Bio Prov) and an acrylic resin as control.
View Article and Find Full Text PDFConsideration of the work environment in a case of an industrial homeworker with allergic contact dermatitis by UV-curing acrylic resin.
Arch Environ Occup Health
January 2025
Department of Oral Epidemiology, Graduate School of Biomedical and Health Sciences, Hiroshima University, Hiroshima-city, Hiroshima, Japan.
We report a case of an industrial homeworker diagnosed with allergic contact dermatitis by UV-curing acrylic resin for crafts. Approximately 2 months after a female in her 40s started producing handicrafts using resin, itchy desquamative erythema and vesicles occurred on her eyelids and palms. The course of the symptoms suggested that her dermatitis was occupational origin.
View Article and Find Full Text PDFShort dentin etching with universal adhesives: effect on bond strength and gingival margin adaptation.
BMC Oral Health
January 2025
Conservative Department, Faculty of Dentistry, Kafr Al Sheikh University, Kafr Al Sheikh, Egypt.
Background: Short dentin etching, a relatively recent technique, aims to improve resin-dentin bonding by preserving hydroxyapatite crystals within the collagen spaces. This study explores short dentin etching's potential in mitigating over-etching issues in deep proximal dentin/cementum margins, an aspect not previously investigated. This study evaluates the microtensile bond strength (μTBS) and marginal adaptation of two universal adhesives using different etch-and-rinse strategies (15-second and 3-second etching) and self-etch strategies, both immediate and post-thermal cycling and mechanical loading.
View Article and Find Full Text PDFGingival margin interfacial microleakage, staining, and push-out strengths of gingival colored composite resins in denture bases.
J Prosthet Dent
January 2025
Professor, Department of Dentistry, Federal University of Santa Catarina (UFSC), Florianópolis, SC, Brazil. Electronic address:
Statement Of Problem: Staining at the gingival margin could impact denture longevity, but the behavior of gingival colored composite resins (GCCs) in this area remains unclear.
Purpose: This in vitro study evaluated surface staining, microleakage, and push-out bond strength at the gingival margin of artificial teeth, comparing two consistencies of GCCs with two resin base materials.
Material And Methods: Specimens included artificial teeth (Ivostar; Ivoclar AG) and two acrylic resin base materials: conventional (Ondacryl; Clássico) and high-impact (Diamond D; Keystone Industries) (n=300).
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!