Phase and structural changes in hydroxyapatite coatings under heat treatment.

Hydroxyapatite (HA) crystallites of smaller size than those formed during the spraying process are found in HA coatings on titanium as a result of the crystallization of the amorphous phase (approximately 630 degrees C) when the coatings are vacuum-heat-treated in the temperature interval 100-1000 degrees C. As the annealing temperature increases within the 630-1000 degrees C range, the size of the crystallites increases, and at 1000 degrees C reaches the size of those formed during the process of spraying. At the same time, at 800 degrees C and above, HA transforms into other calcium phosphate phases (alpha-tricalcium phosphate, beta-tricalcium phosphate, tetracalcium monoxide diphosphate). These phase transformations lead to the increase of coating roughness.