Objectives: Irradiation of enamel with carbon dioxide (CO2) laser energy alters physical and chemical properties of the enamel surface, and these lasers hold promise for conditioning enamel for bonding of adhesive restorations. This laboratory study examined the influence of laser irradiation parameters on the shear bond strength obtained for laser etching using a hybrid composite.
Methods: Standardized surfaces prepared on 110 non-carious intact extracted anterior teeth were exposed to CO2 laser energy (9 different laser exposure parameters) or etched with orthophosphoric acid.
Results: Laser treatment under defined conditions (power density 2380 W/cm2, energy density 23.8 J/cm2) resulted in a bond strength of 30.0 +/- 4.7 MPa, which exceeded that obtained for acid etching (17.9 +/- 4.3 MPa, p < 0.0001). Cohesive failure occurred within the bonding resin in this group.
Significance: These data indicate that CO2 laser etching may enhance the bonding of resin composite to human enamel.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1016/0109-5641(94)90026-4 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Acid resistance and bond strength of calcium-containing adhesive on ename.
Int Dent J
January 2025
Department of Cariology and Operative Dentistry, Graduate School of Medical and Dental Sciences, Institute of Science Tokyo, Bunkyo-ku, Tokyo, Japan.
Introduction And Aims: Marginal sealing by enamel bonding is important to enhance the durability of the restoration and prevent secondary caries after operative procedure. This study aimed to evaluate the enamel acid resistance and bond strength of an experimental calcium-containing adhesive system.
Methods: All materials were provided by Kuraray Noritake Dental, Inc.
Impact of surface pre-treatment on bond strength between cement and zirconia: A systematic review and network meta-analysis.
J Prosthet Dent
January 2025
Associate Professor, Department of Prosthodontics, Dental Branch, Islamic Azad University of Medical Sciences, Tehran, Iran.
Statement Of Problem: The optimal zirconia pretreatment, contingent upon the type of cement used, warrants further research.
Purpose: The purpose of this investigation was to evaluate the influence of various surface pretreatments on the bonding efficacy of cement to zirconia.
Material And Methods: A comprehensive search was conducted across the PubMed, Embase, Scopus, and Web of Science databases for in vitro studies related to bonding with zirconia up to April 2024, supplemented by a manual search.
Bond strength to eroded dentin as per chlorhexidine use for controlling erosive wear or interface aging: an 18-month assay.
Braz Oral Res
January 2025
Universidade de São Paulo - USP, School of Dentistry, Department of Operative Dentistry, São Paulo, SP, Brazil.
The aim of this study was to assess the effect of a chlorhexidine digluconate solution (CHX) applied as an antiproteolytic agent for controlling erosive tooth wear or as part of the adhesive treatment on long-term bond strength to eroded dentin. Dentin specimens were abraded with a 600-grit silicon carbide (SiC) paper for 1 min (sound dentin - S), subsequently treated with 2% CHX for 1 min (with excess removed, followed by a 6-hour rest), and eroded by exposure to Coca-Cola for 5 min, three times a day, for 5 days (CHX-treated and eroded dentin - CHXE), or only eroded (eroded dentin - E). The specimens were acid-etched (15 s), rinsed (30 s), dried (15 s), and rehydrated with 1.
View Article and Find Full Text PDFSystematic evaluation of adhesives for implant fixation in multimodal functional brain MRI.
MAGMA
January 2025
Translational Research Imaging Center (TRIC), Clinic of Radiology, University of Münster, Albert-Schweitzer-Campus 1, building A16, 48149, Münster, Germany.
Objective: Invasive multimodal fMRI in rodents is often compromised by susceptibility artifacts from adhesives used to secure cranial implants. We hypothesized that adhesive type, shape, and field strength significantly affect susceptibility artifacts, and systematically evaluated various adhesives.
Materials And Methods: Thirty-one adhesives were applied in constrained/unconstrained geometries and imaged with T2*-weighted EPI at 7.
Outcome of Er, Cr:YSGG laser and antioxidant pretreatments on bonding quality to caries-induced dentin.
BMC Oral Health
January 2025
Conservative Dentistry Department, Faculty of Oral and Dental Medicine, Future University, Cairo, Egypt.
Background: This study aimed to assess the influence of different pretreatment protocols and antioxidants application on the shear bond strength (SBS) of universal adhesive to sound (SoD) and caries-induced dentin (CID).
Methods: One hundred and twenty posterior teeth had their occlusal enamel removed, then the specimens were divided into two main groups according to dentin substrates; SoD and CID, three subgroups according to pretreatments protocols control (no pretreatment), NaOCl-treated, and Er, Cr:YSGG-treated and two divisions according to antioxidant application (with and without sodium ascorbate (SA) application). All-Bond Universal (ABU) universal adhesives was applied in self-etch (SE) mode then resin composite discs were built.
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!