Purpose: To evaluate the shear bond strength (SBS) of stereolithography (SLA), digital light processing (DLP) manufactured, and computer numerical control (CNC) milled zirconia to veneering ceramic.
Materials And Methods: Rectangular shaped zirconia substrates (10 × 5 × 5 mm) were manufactured through SLA, DLP, and CNC technology separately. Their surface roughness was measured and the surface topography was analyzed by atomic force microscope (AFM). Then the veneering ceramic (5 × 5 × 5 mm) was applied to carry out the SBS test. Failure modes were examined by a scanning electron microscope (SEM). The data of SBS and roughness were statistically analyzed with one-way ANOVA followed by S-N-K post hoc comparisons (a = 0.05).
Results: The surface roughness of the SLA group (0.38 ± 0.03 µm) and the DLP group (0.37 ± 0.04 µm) were both significantly higher than the CNC group (0.16 ± 0.00 µm) (p < 0.001). AFM results revealed irregular surface of SLA and DLP zirconia. No significant difference was found in SBS value of the three groups (p = 0.253). SEM image showed different failure modes including cohesive, adhesive, and mixed failure.
Conclusion: The bonding ability of SLA and DLP zirconia to veneering ceramic were comparable with that of CNC zirconia.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1111/jopr.14034 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Effect of Mushroom, Ozone Gas, and Their Combination as Pretreatment Materials on the Bond Strength of Resin Composite to Dentin.
J Contemp Dent Pract
October 2024
Department of Dental Biomaterials, Faculty of Dental Medicine for Girls, Al-Azhar University, Cairo, Egypt, Orcid: https://orcid.org/0000-0002-3420-4146.
Aim: To assess the effect of mushrooms, ozone gas, and their combination as cavity disinfectants on the bonding strength of composite to dentin.
Materials And Methods: The study was conducted on 40 sound premolar teeth randomly divided into four groups. Group I: control group, Group II: mushroom group, Group III: Ozone group, and Group IV: mushroom + ozone gas (combination) group.
Shear bond strength of vat photopolymerization additive-manufactured zirconia to veneering ceramic.
J Prosthodont
January 2025
Department of Prosthodontics, Shanghai Ninth People's Hospital, Shanghai Jiao Tong University School of Medicine; College of Stomatology, Shanghai Jiao Tong University; National Center for Stomatology; National Clinical Research Center for Oral Diseases; Shanghai Key Laboratory of Stomatology; Shanghai Research Institute of Stomatology, Shanghai, PR China.
Purpose: To evaluate the shear bond strength (SBS) of stereolithography (SLA), digital light processing (DLP) manufactured, and computer numerical control (CNC) milled zirconia to veneering ceramic.
Materials And Methods: Rectangular shaped zirconia substrates (10 × 5 × 5 mm) were manufactured through SLA, DLP, and CNC technology separately. Their surface roughness was measured and the surface topography was analyzed by atomic force microscope (AFM).
Different Composite Veneer Surface Preparations for Metal Orthodontic Bracket Bonding: An In Vitro Study.
Int J Dent
January 2025
Department of Orthodontics, School of Dentistry, Mashhad University of Medical Sciences, Mashhad, Iran.
This research aimed to assess the shear bond strength (SBS) of metal brackets bonded to composite veneers using different surface preparations. One-hundred composite disks were divided into 10 different groups whereby each group combines a surface preparation (roughening or no roughening), etching agent (37% phosphoric or 9.5% hydrofluoric acid), adhesive protocol (self-etch or total-etch), and bonding agent (with or without G-Premio Bond).
View Article and Find Full Text PDFEffect of Different Working Settings of Sandblasting on Resin Composite Repair Bond Strength.
Materials (Basel)
January 2025
Department of Preventive Dentistry, Periodontology and Cariology, University Medical Center Göttingen, 37075 Göttingen, Germany.
To investigate the effect of different sandblasting settings on the shear bond strength (SBS) in the repair of resin composite, specimens (resin composite, enamel, and dentin; each group = 16) were sandblasted by varying the parameters of air pressure (0.2/0.3/0.
View Article and Find Full Text PDFEffect of Air Particle Abrasion and Primers on Bond Strength to 3D-Printed Crown Materials.
Materials (Basel)
January 2025
Division of Biomaterials, School of Dentistry, University of Alabama at Birmingham, Birmingham, AL 35209, USA.
Two 3D-printed crown materials (Crown and Ceramic Crown) were examined to determine the best surface treatment and primers for bonding. Discs of the two materials were printed and mounted with their "intaglio" surfaces untouched. Half the specimens from each group were sandblasted with 50 µm alumina.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!