Effect of carbon nanotubes and zinc oxide on electrical and mechanical properties of polyvinyl alcohol matrix composite by electrospinning method.

In this study, polymer composite nanofibers and thin membranes were synthesized using Carbon Nanotubes (CNTs) and Zinc Oxide (ZnO) as fillers in a Polyvinyl Alcohol (PVA) matrix, aiming to evaluate their electrical and mechanical properties. The composite nanofibers and thin membranes were prepared by incorporating different weight ratios of CNTs and ZnO into the PVA matrix using electrospinning and solution casting techniques, respectively. Solutions were prepared by mixing specific weight ratios of PVA, ZnO, and CNTs, followed by magnetic stirring and ultrasonication for homogenization. Electrospinning was performed at 20 kV with a syringe-to-collector distance of 14.5 cm at flow rate of 2.4 ml/hr. The composites were characterized using FTIR spectroscopy and Scanning Electron Microscopy (SEM). The PVA/5%ZnO/0.5%CNT composite exhibited the highest dielectric constant of 10.3 at high frequencies, while PVA/5%CNT showed the highest capacitance of 31.1 pF at 2 MHz. The maximum AC conductivity of 2.72 × 10S/m was also observed for the PVA/5%ZnO/0.5%CNT composite. Mechanical testing revealed significant improvements in Young's modulus, stress yield, and load yield, with PVA/5%CNT achieving a Young's modulus of 387.12 MPa and a stress yield of 6.92 MPa. The addition of ZnO and CNT fillers resulted in enhanced electrical and mechanical properties, making these composites suitable for applications in microelectronic devices and packaging materials.