Three-Dimensional Micromechanical Modeling of Martensite Particle Size Effects on the Deformation Behavior of Dual-Phase Steels.

The objective of this study was to examine the influence of martensite particle size on the formation of stress and strain in microstructures of dual-phase steels. In order to achieve this objective, the 3D representative volume element (RVE) method was utilized. Particle size distributions were obtained from the microstructures of DP600 and DP1000 dual-phase steels as they actually exist. Virtual dual-phase steel microstructures were generated according to the above distribution and subsequent validation analyses were performed. In the subsequent phase, microstructures of varying martensite particle sizes (1 µm, 1.98 µm, 3 µm for DP600 and 1.15 µm, 2 µm, 3 µm for DP1000) were formed, and the effects of particle size on deformation behavior under tensile loads were determined. The findings indicated that an increase in martensite particle size resulted in a reduction in tensile strength, accompanied by an increase in deformation amount.