Elemental analysis and micromorphological patterns of tooth/restoration interface of three ion-releasing class V restorations.

Objectives: To evaluate and compare the ion-releasing capability of three different restorative systems at the restoration/tooth interface elemental analysis using energy-dispersive X-ray technique. Additionally, micromorphological patterns of the restoration/tooth interfaces was investigated.

Materials And Methods: Eighteen freshly extracted sound human premolars were collected for the study. The premolars were randomly assigned into 3 groups (n = 6) based on the type of restorative materials used: Giomer (Beautifill II), ion-releasing composite (Activa Presto), and RMGI (Riva Light Cure). Half of the specimens in each group were tested after 24 h (the "immediate group"), while the remaining half were tested after 6 months of storage in deionized water (the "delayed group"). Standardized box-shaped cavities along the cervical area of teeth crowns and restored them with the assigned restorative material following manufacturers' instructions. The specimens were sectioned buccolingually into 2 halves. One half of each specimen was subjected to elemental analysis using energy-dispersive X-ray technique (EDX), while the remaining half was sputter coated and underwent micromorphological analysis of the restoration/tooth interface using a scanning electron microscope (SEM). The collected data from elemental analysis test were tabulated and subjected to statistical analysis.

Results: The two-way ANOVA test showed significant differences in both phosphorus and calcium levels among the tested restorative systems (p < 0.05). In the immediate subgroup, RMGI recorded the highest phosphorus level (0.1527), followed by the ion-releasing composite (0.1172), while Giomer exhibited the least levels (0.0326) (p < 0.05). The ion-releasing composite group had the highest calcium level (0.2797), followed by RMGI (0.248), and Giomer (0.2385) respectively (p < 0.05). In the delayed subgroups, Giomer recorded the highest phosphorus level (0.1526), followed by the ion-releasing composite (0.1058), and RMGI group (0.0466) respectively (p < 0.05). RMGI had the highest calcium level (0.2801), followed by the ion-releasing composite (0.2659), and Giomer had the lowest level (0.1792) (p < 0.05). The micromorphological analysis of the restoration/tooth interfaces showed good adaptation between the composite and tooth substrate in different restorative groups.

Conclusions: The ion-releasing capability of the three restorative systems appears to be comparable. The rate of mineral release and diffusion is affected by time and composition.