Abiotic degradation and accelerated ageing of microplastics from biodegradable and recycled materials in artificial seawater.

Microplastics (MPs) are considered one of the most widespread pollutants in all ecosystems worldwide. In the environment, MPs can undergo hydrolysis and/or oxidation, resulting in the release of low-molecular weight degradation products, along with additives, and adsorbed organic pollutants. In this study, the morphological, chemical, and thermal changes of microplastics obtained from two biodegradable plastics, polylactic acid and Mater-Bi®, and a recycled plastic, recycled-polyethylene terephthalate, were examined after accelerated ageing under photo-oxidative conditions in synthetic seawater in a Solarbox system, and after thermal treatment in the dark. Thermal properties were studied by thermogravimetric analysis, differential scanning calorimetry, and evolved gas analysis-mass spectrometry. Compositions and changes of chemical components of the polymers were evaluated by attenuated total reflection-Fourier transform infrared spectroscopy and pyrolysis-gas chromatography-mass spectrometry. The leachable fractions and degradation products released in synthetic seawater by degraded MPs were characterized by gas chromatography-mass spectrometry. This study allowed us to identify hydrolysis as the main degradation pathway of the polymers under analysis, and to characterize not only the oligomers and degradation products released in the water as a consequence of degradation, but also additives used in plastic item formulations. This study improves our understanding of these polymers' behavior under accelerated ageing conditions.