Investigating the Effects of Transition Metals and Activated Carbon on Hydrogenation Characteristics of Severely Deformed ZK60 Processed by High-Energy Ball Milling.

The synergic effects of activated carbon and transition metals on the hydrogenation characteristics of commercial ZK60 magnesium alloy were investigated. Severe plastic deformation was performed using equal-channel angular pressing with an internal die angle of 120° and preheating at 300 °C. The ZK60 alloy samples were processed for 12 passes using route B. The deformed ZK60 alloy powder was blended with activated carbon and different concentrations of transition metals (Ag, Pd, Co, Ti, V, Ti) using high-energy ball milling for 20 h at a speed of 1725 rpm. The amount of hydrogen absorbed and its kinetics were calculated using Sievert's apparatus at the higher number of cycles at a 300 °C ab/desorption temperature. The microstructure of the powder was analyzed using an X-ray diffractometer and scanning electron microscope. The results indicated that 5 wt% activated carbon presented the maximum hydrogen absorption capacity of 6.2 wt%. The optimal hydrogen absorption capacities were 7.1 wt%, 6.8 wt%, 6.7 wt%, 6.64 wt%, 6.65 wt%, and 7.06 wt% for 0.5 Ag, 0.3 Co, 0.1 Al, 0.5 Pd, 2 Ti, and 0.5 V, respectively. The hydrogen absorption capacities were reduced by 35.21%, 26.47%, 41.79%, 21.68%, 26.31%, and 26.34% after 100 cycles for 5C0.5Ag, 5C0.3Co, 5C0.1Al, 5C0.5Pd, 2Ti, and 5C0.5V, respectively. Hydrogen absorption kinetics were significantly improved so that more than 90% of hydrogen was absorbed within five minutes.