Comparative Evaluation of Mechanical and Physical Properties of Mycelium Composite Boards Made from with Various Ratios of Corn Husk and Sawdust.

Mycelium-based composites (MBCs) exhibit varied properties as alternative biodegradable materials that can be used in various industries such as construction, furniture, household goods, and packaging. However, these properties are primarily influenced by the type of substrate used. This study aims to investigate the properties of MBCs produced from strain CMU-NK0427 using different ratios of sawdust to corn husk in the development of mycelium composite boards (MCBs) with thicknesses of 8, 16, and 24 mm. The results indicate that variations in the ratios of corn husk to sawdust and thickness affected the mechanical and physical properties of the obtained MCBs. Reducing the corn husk content in the substrate increased the modulus of elasticity, density, and thermal conductivity, while increasing the corn husk content increased the bending strength, shrinkage, water absorption, and volumetric swelling. Additionally, an increase in thickness with the same substrate ratio only indicated an increase in density and shrinkage. MCBs have sound absorption properties ranging from 61 to 94% at a frequency of 1000 Hz. According to the correlation results, a reduction in corn husk content in the substrate has a significant positive effect on the reduction in bending strength, shrinkage, and water absorption in MCBs. However, a decrease in corn husk content shows a strong negative correlation with the increase in the modulus of elasticity, density, and thermal conductivity. The thickness of MCBs with the same substrate ratio only shows a significant negative correlation with the modulus of elasticity and bending strength. Compared to commercial boards, the mechanical (bending strength) and physical (density, thermal conductivity, and sound absorption) properties of MCBs made from a 100% corn husk ratio are most similar to those of softboards and acoustic boards. The results of this study can provide valuable information for the production of MCBs and will serve as a guide to enhance strategies for further improving their properties for commercial manufacturing, as well as fulfilling the long-term goal of eco-friendly recycling of lignocellulosic substrates.