Surface-anchored N-based functional groups driven photoactivity of SrTiO.

Surface modification, including the anchoring of functional groups is a popular method to increase the photocatalytic activity of semiconductor photocatalysts. These species can trap excited electrons, thus prolonging the life of the charge carriers. N-containing functional groups are suitable for this purpose due to their high electron density. Here, we report a facile synthesis method for preparing interfacial N-based functional groups-modified and nitrogen-doped SrTiO photocatalysts. Among the modified samples (with 0.42-11.14 at.% nominal nitrogen content), the one with 7.71 at.% nitrogen showed 6.4 times higher photooxidation efficiency for phenol and 2.2 times better photoreduction efficiency for CO conversion than the unmodified SrTiO reference. Characterization results showed that using a low amount of nitrogen source resulted in low but measurable nitrogen doping, which did not significantly affect the photocatalytic activity. The formation of surface amine groups was significant even at lower initial nitrogen concentrations, while higher amounts of nitrogen source gradually resulted in the incorporation of nitrogen in higher amounts. Surface amine groups decreased the recombination of charge carriers, resulting in increased photocatalytic activity.