Framework's marginal adaptation evaluation of fixed partial denture using conventional and digital impression techniques.

Purpose: To evaluate the marginal and internal misfit of fixed partial denture zirconia frameworks developed from conventional impression and intraoral scanning, before and after being subjected to the thermal cycle of the covering ceramic.

Methods: A three-elements fixed partial denture was prepared, molded, and poured with polyurethane. Group CI (n= 7) was impressed by the conventional technique with polyvinyl siloxane material, and the plaster models scanned on the inEosX5 bench scanner. Group DI (n=07) was scanned using the CEREC Bluecam intraoral scanner. The models and images obtained were sent to the laboratory and the frameworks were made using zirconia blocks. After this, they were subjected to the ceramic thermal cycle, simulating the ceramic application. Marginal and internal misfits of the frameworks were measured before (T1) and after (T2) thermal cycle simulation using the replica technique in an optical microscope. Statistical analysis was performed using the mixed effects of linear model tests and comparisons.

Results: There were no statistical differences for axial misfit. Significant differences were found between the groups for occlusal, vertical, horizontal, and absolute misfit, where group CI had higher values than group DI (P< 0.001). At the time, there was a statistical difference only in the absolute misfit, where T1 had lower values than T2. The misfit in group CI was greater than in group DI; however, the average misfit values found are low and considered clinically acceptable.

Clinical Significance: Knowing marginal and internal misfit is an important step to consolidating digital impressions in fixed partial dentures, implying a secure use of this technique.