Wear characteristics of resin-based luting agents used in the bonded CAD-CAM resin blocks.

This study aimed to investigate the wear and microhardness of luting agents and computer-aided design-computer-aided manufacturing (CAD-CAM) resin blocks, and to compare the wear characteristics of resin-based luting agents used in bonded specimens of CAD-CAM resin blocks. After three-body wear test, the amount of wear and Vickers hardness were measured and Pearson's correlation coefficient was calculated. The lowest amount of wear and the highest Vickers hardness values were obtained for Estecem II. Filler loss was observed in five composite resin cements. A strong negative correlation was observed in the luting agents between the amount of wear and Vickers hardness value (r=-0.874, p<0.0001). Additionally, a strong positive correlation was observed between the amount of wear of the bonded specimen and amount of luting agent used alone (r=0.943, p<0.0001). To conclude, the wear resistance of the luting agent used in the bonded specimen was significantly influenced by the bonding between the filler and matrix resin.