Eco-Friendly Waterborne Polyurethane Coating Modified with Ethylenediamine-Functionalized Graphene Oxide for Enhanced Anticorrosion Performance.

This study explores the potential of graphene oxide (GO) as an additive in waterborne polyurethane (WPU) resins to create eco-friendly coatings with enhanced anticorrosive properties. Traditionally, WPU's hydrophilic nature has limited its use in corrosion-resistant coatings. We investigate the impact of incorporating various GO concentrations (0.01, 0.1, and 1.3 wt%) and functionalizing GO with ethylenediamine (EDA) on the development of anticorrosive coatings for carbon steel. It was observed, by potentiodynamic polarization analysis in a 3.5% NaCl solution, that the low GO content in the WPU matrix significantly improved anticorrosion properties, with the 0.01 wt% GO-EDA formulation showing exceptional performance, high E (-117.82 mV), low i (3.70 × 10 A cm), and an inhibition corrosion efficiency (η) of 99.60%. Raman imaging mappings revealed that excessive GO content led to agglomeration, creating pathways for corrosive species. In UV/condensation tests, the 0.01 wt% GO-EDA coating exhibited the most promising results, with minimal corrosion products compared to pristine WPU. The large lateral dimensions of GO sheets and the cross-linking facilitated by EDA enhanced the interfacial properties and dispersion within the WPU matrix, resulting in superior barrier properties and anticorrosion performance. This advancement underscores the potential of GO-based coatings for environmentally friendly corrosion protection.