Reactive Blue MEBF 222 dye and textile wastewater treatment using metal-doped cobalt and nickel perovskites by batch and column adsorption process.

Water contamination is a serious issue that has an impact on the whole globe. In the current work, adsorption technique was used to remove synthetic Reactive Blue MEBF 222 textile dye utilizing Cd-doped Co (CoCdFeO), Zn-doped Co (CoZnFeO), Cr-doped Co (CoCrFeO), Zn-doped Ni (NiZnFeO), and Cr-doped Ni (NiCrFeO) perovskites, synthesized by sol-gel auto-combustion approach. According to the findings of batch adsorption studies, maximum adsorption was observed at pH 3 (45.62 mg/g), 0.01 g/50 ml dosage (36.67 mg/g), 60 min (14.31 mg/g), 100 ppm dye concentration (47.41 mg/g), and 308 K (35.96 mg/g) for CoCdFeO; at 3 pH (42.94 mg/g), 0.01 g/50 ml dosage (35.33 mg/g), 60 min (12.88 mg/g), 100 ppm dye concentration (40.52 mg/g), and 308 K (31.31 mg/g) for CoZnFeO; at 2 pH (38.82 mg/g), 0.01 g/50 ml dosage (32.20 mg/g), 60 min (11.98 mg/g), 100 ppm dye concentration (33.54 mg/g), and 308 K (29.34 mg/g) for CoCrFeO; at 2 pH (34.97 mg/g), 0.01 g/50 ml dosage (30.41 mg/g), 60 min (10.46 mg/g), 100 ppm dye concentration (27.19 mg/g), and 308 K (26.12 mg/g) for NiZnFeO; and at 2 pH (31.22 mg/g), 0.01 g/50 ml dosage (25.04 mg/g), 60 min (9.48 mg/g), 100 ppm dye concentration (21.73 mg/g), and 308 K (23.61 mg/g) for NiCrFeO. The pseudo-second-order model showed good fitness for adsorption kinetic data. Electrolytes, detergents/surfactants, and heavy metal ions had a substantial impact on the adsorption potential. The column adsorption experiments demonstrated optimal bed height, flow rate, and intake dye concentration to be 3 cm, 1.8 ml/min, and 70 mg/l, respectively, in the column experiment. With an adsorption capacity of 44.1 mg/g, reactive blue (RB) 222 dye was able to achieve its maximum adsorption. Detailed desorption of RB 222 dye was also achieved. The novelty of this adsorption method lies in its eco-friendliness, ease of handling, and cost-effectiveness.