Evaluation of the physical properties of bromelain-modified biodentine for direct pulp capping.

Background: This study aims to evaluate the compressive strength, solubility, radiopacity, and flow of Bromelain (BR)-modified Biodentine (BD) for direct pulp capping (DPC). This is suggested to determine the impact of BR on the physical properties of BD.

Methods: Eighty samples were prepared according to the ISO and ADA specifications and evaluated for compressive strength, solubility, radiopacity, and flow. The compressive strength was evaluated at 24 h and 21 days via a universal testing machine. The solubility was determined by weight loss after 24-hours immersion in deionized water. Radiopacity was assessed via X-ray with aluminum step-wedges, and flow was measured by the diameter of the discs under a standard weight. Independent sample t-tests were used to statistically assess the data. A significance level of 5% was considered.

Results: The compressive strength was 41.08 ± 1.84 MPa for BD and 40.92 ± 1.80 MPa for BR + BD after 24 h, and 88.93 ± 3.39 MPa for BD and 87.92 ± 3.76 MPa for BR + BD after 21 days, with no significant differences. Solubility was slightly greater in the BR + BD (2.75 ± 0.10%) compared to BD (2.62 ± 0.25%), but not significantly different. The radiopacity was similar between BD (2.82 ± 0.11 mm) and BR + BD (2.73 ± 0.10 mm). BR + BD resulted in significantly greater flow (9.99 ± 0.18 mm) than did BD (9.65 ± 0.27 mm) (p ≤ 0.05).

Conclusion: BR-modified BD maintains BD's physical properties, with improved flow, making it a promising DPC agent that warrants further study.