Facilitating Oriented Dense Deposition: Utilizing Crystal Plane End-Capping Reagent to Construct Dendrite-Free and Highly Corrosion-Resistant (100) Crystal Plane Zinc Anode.

Dendrite growth and corrosion issues have significantly hindered the usability of Zn anodes, which further restricts the development of aqueous zinc-ion batteries (AZIBs). In this study, a zinc-philic and hydrophobic Zn (100) crystal plane end-capping reagent (ECR) is introduced into the electrolyte to address these challenges in AZIBs. Specifically, under the mediation of 100-ECR, the electroplated Zn configures oriented dense deposition of (100) crystal plane texture, which slows down the formation of dendrites. Furthermore, owing to the high corrosion resistance of the (100) crystal plane and the hydrophobic protective interface formed by the adsorbed ECR on the electrode surface, the Zn anode demonstrates enhanced reversibility and higher Coulombic efficiency in the modified electrolyte. Consequently, superior electrochemical performance is achieved through this novel crystal plane control strategy and interface protection technology. The Zn//VO cells based on the modified electrolyte maintained a high-capacity retention of ≈80.6% after 1350 cycles, corresponding to a low-capacity loss rate of only 0.014% per cycle. This study underscores the importance of deposition uniformity and corrosion resistance of crystal planes over their type. And through crystal plane engineering, a high-quality (100) crystal plane is constructed, thereby expanding the range of options for viable Zn anodes.