Influence of Battery Levels in Cordless LED Light-curing Units on Properties of Resin Cement and Glass Fiber Post Retention.

Purpose: This study aimed to assess the impact of battery levels in single-peak and multi-peak light-curing units (LCUs) on irradiance, and their effects on glass fiber post push-out bond strength to root dentin and the degree of conversion of dual-cure universal resin cement.

Methods And Materials: Sixty bovine roots underwent endodontic treatment and were randomly distributed into 6 groups (n=10), formed by combining two LCUs (single-peak and multipeak) and three battery levels (100%, 50%, and 10%). A spectrophotometer measured irradiance (mW/ cm2) and spectral irradiance (mW/cm2/nm). Push-out bond strength (PBS) tests occurred at three root regions (cervical, middle, and apical), with optical and scanning electron microscopy for failure mode analysis. Degree of conversion (DC) was evaluated across the root regions. Data were analyzed using two-way repeated measures ANOVA and the Tukey HSD test. The Fisher exact test verified failure modes (α=0.05).

Results: As multipeak LCU battery levels decreased, emitted irradiance also diminished, with notable PBS reductions in the apical thirds. Failure modes were influenced by different conditions, primarily exhibiting mixed modes. Battery levels significantly impacted DC in the multipeak LCU, particularly in the cervical region, while the single-peak LCU exhibited DC reduction at the 10% battery level in the cervical region.

Conclusions: Emitted irradiance, resin cement DC, and glass fiber post bond strength to root dentin may be influenced by varying cordless LCUs and battery levels.