Influence of Carbonyl Iron Particles (CIP) and Glass Microspheres on Thermal Properties of Poly(lactic acid) (PLA).

In this investigation, composite poly(lactic acid) (PLA) systems of hollow glass microspheres (MS) and carbonyl iron particles (CIP) were processed and characterized to investigate the effects of using conductive and insulating particles as additives in a polymer system. PLA-MS and PLA-CIP were set at the two levels of 3.94 and 7.77 vol.% for each particle type to study the effects of the particle material type and loading on neat PLA's thermal properties. It was observed during the twin-screw extrusion that the addition of CIP greatly decreased the viscosity of the PLA melt during processing. Correlations determined using thermogravimetric analysis, differential scanning calorimetry, thermal conductivity, and shear rheology provided insights into how thermal stability was affected. The incorporation of MS and CIP altered thermal properties such as the glass transition temperature (T), melting temperature (T), and cold crystallization temperature (T). The metal CIP-filled systems had large increases in their thermal conductivity values and viscoelastic transitions compared to those with PLA that were correlated with the observed overheating during extrusion.