Wear Performance Evaluation of Polymer Overlays on Engine Bearings.

Modern engine bearing materials encounter the challenge of functioning under conditions of mixed lubrication, low viscosity oils, downsizing, start-stop engines, potentially leading to metal-to-metal contact and, subsequently, premature bearing failure. In this work, two types of polymer overlays were applied to the bearing surface to compensate for extreme conditions, such as excessive loads and mixed lubrication. Two different polymer overlays, created through a curing process on a conventional engine bearing surface with an approximate thickness of 13 µm, were investigated for their friction and wear resistances under a 30 N load using a pin-on-disc setup. The results indicate that the newly developed polymer overlay (NDP, PAI-based coating) surface has a coefficient of friction (COF) of 0.155 and a wear volume loss of 0.010 cm. In contrast, the currently used polymer overlay (CPO) in this field shows higher values with a COF of 0.378 and a wear volume loss of 0.024 cm, which is significantly greater than that of the NDP. It was found that, in addition to accurately selecting the ratios of solid lubricants, polymer resins, and wear-resistant hard particle additives (metal powders, metal oxides, carbides, etc.) within the polymer coating, the effective presence of a transfer film providing low friction on the counter surface also played a crucial role.