Study on Fast Liquefaction and Characterization of Produced Polyurethane Foam Materials from Moso Bamboo.

Although bamboo is widely distributed in Japan, its applications are very limited due to its poor combustion efficiency for fuel. In recent years, the expansion of abandoned bamboo forests has become a social issue. In this research, the possibility of a liquefaction process with fast and efficient liquefaction conditions using moso bamboo as raw material was examined. Adding 20 wt% ethylene carbonates to the conventional polyethylene glycol/glycerol mixed solvent system, the liquefaction time was successfully shortened from 120 to 60 min. At the same time, the amount of sulfuric acid used as a catalyst was reduced from 3 wt% to 2 wt%. Furthermore, polyurethane foam was prepared from the liquefied product under these conditions, and its physical properties were evaluated. In addition, the filler effects of rice husk biochar and moso bamboo fine meals for the polyurethane foams were characterized by using scanning electron microscopy (SEM) and thermogravimetry and differential thermal analysis (TG-DTA), and the water absorption and physical density were measured. As a result, the water absorption rate of bamboo fine meal-added foam and the thermal stability of rice husk biochar-added foam were improved. These results suggested that moso bamboo meals were made more hydrophilic, and the carbon content of rice husk biochar was increased.