Terpyridine-Decorated Polymer Nanosphere Latex: Template Nanocarriers for the Synthesis of Cu-CeO Hollow Spheres.

Water-soluble polymers with the ability to complex metal ions through complexing ligands have attracted significant interest in diverse domains, such as optical or catalyst applications. In this paper, we successfully synthesized, through a one-pot process combining polymerization-induced self-assembly and reversible addition-fragmentation chain transfer polymerization, aqueous dispersions of terpyridine-decorated poly[poly(ethylene glycol)methyl ether methacrylate]--poly(methyl methacrylate) (tpy-PPEGMA--PMMA) amphiphilic block copolymers. The formation of well-defined amphiphilic block copolymers and their self-assembly led to nanosphere latex with the hydrodynamic diameters increasing from 17 to 52 nm and the length of the copolymers increasing from 21,000 to 51,000 g·mol. These aqueous dispersed tpy-PPEGMA--PMMA nanospheres effectively complex metal ions, such as Cu, in a stoichiometric ratio of 2:1. Subsequently, these metal-complexed nanospheres were employed as soft template nanocarriers to control, on the nanometer scale, the dispersion of metal on a nanostructured support. This is exemplified by the synthesis of copper supported on cerium oxide hollow spheres (Cu-CeO) using Cu-tpy-PPEGMA--PMMA as template nanocarriers and CeO nanoparticles. This novel assembly engineering strategy for the preparation of atomically dispersed metal on a nanostructured support was highlighted through the utilization of Cu-CeO hollow spheres as an electrocatalyst for the nitrate reduction reaction (NORR) to NH. These encouraging outcomes emphasize the potential of metal-metal oxide-nanostructured materials to treat contaminated water sources with nitrate while allowing the green production of ammonia.