Objectives:  The purpose of the present study was to investigate the created roughness and cell attachment of intact teeth (C), obturated teeth with bioceramic (BR), or epoxy resin (AH) after root resection using piezoelectric ultrasonic and carbide bur.

Materials And Methods:  Three groups of first mandibular premolars were used in the present study: control group (without any preparation or obturation) (C); second group was obturated with an epoxy resin sealer (AH, AH Plus Jet); and finally, the third one was obturated with a bioceramic sealer (BR, BioRoot RCS). All teeth were incubated for 4 months at 37°C. After that, the samples were sectioned using tungsten carbide bur or piezoelectric ultrasonic. Roughness and then cell attachment of periodontal ligament cells on the sectioned surfaces were investigated by profilometer and confocal microscope, respectively.

Statistical Analysis:  Data were statistically analyzed using one-way analysis of variance.

Results:  After root resection, no significant difference was found between the roughness among the three groups sectioned using the piezoelectric technique ( > 0.05). In contrast, concerning the sectioned samples by burs, C demonstrated a rougher surface compared with BR ( < 0.05). There was a significant higher cell attachment in BR compared with AH in the piezoelectric groups ( = 0.047), while no statistically significant difference was found between the groups sectioned with bur ( > 0.05).

Conclusion:  Dentists are now focused on the use of calcium silicate-based sealers due to their bioactivity. The present study advises dentists to use bioceramic sealer which could improve the dentin characteristics which ameliorate the cell attachment.

Download full-text PDF

Source
http://dx.doi.org/10.1055/s-0044-1788319DOI Listing

Publication Analysis

Top Keywords

roughness cell
12
root resection
12
cell attachment
12
epoxy resin
8
piezoelectric ultrasonic
8
bioceramic sealer
8
effectiveness sectioning
4
sectioning method
4
method filling
4
filling materials
4

Similar Publications

Effective modifications for the buried interface between self-assembled monolayers (SAMs) and perovskites are vital for the development of efficient, stable inverted perovskite solar cells (PSCs) and their tandem photovoltaics. Herein, an ionic-liquid-SAM hybrid strategy is developed to synergistically optimize the uniformity of SAMs and the crystallization of perovskites above. Specifically, an ionic liquid of 1-butyl-3-methyl-1H-imidazol-3-iumbis((trifluoromethyl)sulfonyl)amide (BMIMTFSI) is incorporated into the SAM solution, enabling reduced surface roughness, improved wettability, and a more evenly distributed surface potential of the SAM film.

View Article and Find Full Text PDF

Introduction: α-Calcium sulfate hemihydrate (α-CSH) is a widely used artificial bone graft material, but it suffers from rapid deterioration and limited osteoinductivity. This study aims to develop composite cements by combining treated dentin matrix (TDM) with α-CSH to enhance osteogenic properties for the healing of bone deformities.

Methods: The composite cements were prepared by mixing treated dentin matrix (TDM) with α-calcium sulfate hemihydrate (α-CSH) and characterized for their mechanical, morphological, and chemical properties using a universal mechanical testing machine, scanning electron microscopy (SEM), X-ray diffraction (XRD), and Fourier-transform infrared (FTIR) spectroscopy.

View Article and Find Full Text PDF

Enhancement of polycaprolactone nanofiber film performance by hydrogen bonding interactions with chitosan for food packaging.

Int J Biol Macromol

January 2025

Department of Food Science and Technology, Sunchon National University, Suncheon, Jeonnam 57922, Republic of Korea; Bio-Healthcare Research and Analysis Center, Sunchon National University, Suncheon, Jeonnam 57922, Republic of Korea; Glocal University Project Team, Sunchon National University, 255 Jungangno, Suncheon 57922, Jeonnam, Republic of Korea. Electronic address:

Hybrid environmentally friendly nanocomposite films were synthesized via electrospinning using polycaprolactone (PCL) and chitosan (CH). The resulting nanofiber films displayed a homogeneous fibrous microstructure with average diameters between 250-270 nm. Molecular simulation experiments revealed a progressive increase in hydrogen bonding over time.

View Article and Find Full Text PDF

Microplastics (MP) are suitable substrates for the colonization of harmful microalgal cells and the adsorption of their lipophilic compounds including phycotoxins. Moreover, such interactions likely change as physical-chemical characteristics of the MP surface are gradually modified during plastic degradation in aquatic environments. Using a combination of innovative laboratory experiments, this study systematically investigated, for the first time, the influence of various MP characteristics (polymeric composition, shape, size, and/or surface roughness) on its capacity to carry both living harmful algal cells and dissolved phycotoxins.

View Article and Find Full Text PDF

Perovskite/silicon tandem solar cells (TSCs) are promising candidates for commercialization due to their outstanding power conversion efficiencies (PCEs). However, controlling the crystallization process and alleviating the phases/composition inhomogeneity represent a considerable challenge for perovskite layers grown on rough silicon substrates, ultimately limiting the efficiency and stability of TSC. Here, this study reports a "halide locking" strategy that simultaneously modulates the nucleation and crystal growth process of wide bandgap perovskites by introducing a multifunctional ammonium salt, thioacetylacetamide hydrochloride (TAACl), to bind with all types of cations and anions in the mixed halide perovskite precursor.

View Article and Find Full Text PDF

Want AI Summaries of new PubMed Abstracts delivered to your In-box?

Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!