The Effect of Rapeseed Oil Biopolyols and Cellulose Biofillers on Selected Properties of Viscoelastic Polyurethane Foams.

This paper presents the results of research on polyurethane viscoelastic foams (PUVFs) modified with biomaterials. This investigation looked at the effect of the biomaterials on the foaming processes, as well as the acoustical and selected physical-mechanical properties of the foams. Various types of rapeseed oil biopolyols and microcellulose were used to modify the materials. The analysis of properties covered a reference biopolyol-free sample and materials containing 10 wt.%, 20 wt.%, and 30 wt.% of different types of biopolyols in the mixture of polyol components. The biopolyols differed in terms of functionality and hydroxyl value (OH). Next, a selected formulation was modified with various microcellulose biofillers in the amount of 0.5-2 wt.%. The PUVFs, with apparent densities of more than 210 kg/m and open-cell structures (more than 85% of open cells), showed a slow recovery to their original shape after deformation when the pressure force was removed. They were also characterized by a tensile strength in the range of 156-264 kPa, elongation at break of 310-510%, hardness of 8.1-23.1 kPa, and a high comfort factor of 3.1-7.1. The introduction of biopolyols into the polyurethane system resulted in changes in sound intensity levels of up to 31.45%, while the addition of fillers resulted in changes in sound intensity levels of up to 13.81%.