Improvement of optical and structural properties of ZIF-8 by producing multifunctional Zn/Co bimetallic ZIFs for wastewater treatment from copper ions and dye.

In the paper, high specific surface area (SSA) mono and bimetallic zeolitic imidazolate frameworks (ZIFs) based on zinc and cobalt metals are successfully synthesized at room temperature using different ratios of Zn to Co salts as precursors and ammonium as a solvent to tailor the properties of the produced ZIF and optimize the efficiency of the particles in water treatment from dye and copper ions, simultaneously. The results declare that monometallic and bimetallic ZIF microparticles are formed using ammonium and the tuning of pore sizes and also increasing the SSA by inserting the Co ions in Zn-ZIF particles is accessible. It leads to a significant increase in the thermal stability of bimetallic Zn/Co-ZIF and the appearance of an absorption band in the visible region due to the existence of Co in the bimetallic structures. The bandgap energies of bimetallic ZIFs are close to that of the monometallic Co-ZIF-8, indicating controlling the bandgap by Co ZIF. Furthermore, the ZIFs samples are applied for water treatment from copper ions (10 and 184 ppm) and methylene blue (10 ppm) under visible irradiation and the optimized multifunctional bimetallic Zn/Co ZIF is introduced as an admirable candidate for water treatment even in acidic conditions.