Biowaste Valorization of Palm Tree L. for Nanocellulose Production.

The desire to reduce reliance on oil resources arises from the concerns about carbon footprint and nonrenewability. Conversely, the global presence of over 100 million palm trees poses a significant challenge due to the substantial amount of biowaste generated annually. Additionally, the use of nanocellulose (NC) as a cost-effective material is steadily gaining recognition for its growing adaptability over time. The main goal of this study is to biosynthesized NC from Iraqi date palm leaves waste with low-concentration acid-alkali treatment. The date palm leaves waste yields 20 g of NC from 100 g of leaves before acid hydrolysis treatment. The chemical components of biosynthesized NC were 47.90%, 26.78%, and 24.67% for -cellulose, hemicellulose, and lignin, respectively. In order to study their properties, NC from raw date palm leaves was studied by microscopic techniques such as scanning electron microscopy (SEM), energy dispersive X-ray (EDX) spectroscopy, and atomic force microscope (AFM). SEM results revealed rod-like structured NC as well as combined long-fine fibrous structures rather than compacted bundles with sizes ranging between 31 and 74 nm. With EDX, all spectra exhibit the peaks of carbon and oxygen as the main elements with 63.8% and 10.44%, respectively, in their compositions, which relate to the typical composition of cellulose. The 3D image of AFM NC with a tapping mode presented a highly uniform distribution of NC with a size of ∼15 nm. The statistical roughness analysis shows that the obtained roughness average is 7.20 nm with the root-mean-square roughness value of 21.56 nm, which corresponded relatively with the micrographs of SEM. The results of this study demonstrate the promise of using date palm waste as raw material to produce NC as green nanocomposite from biodegradable nanomaterials for water purification and sustained drug delivery for biomedical applications. In this regard and because of the insufficient reports about the extraction of NC from palm tree leaves waste, the objective of this study was designed to fabricate NC biologically from fibers sourced from the waste of Iraqi date palm leaves that left in agricultural lands or burned, which can be an ecological and health problem as a bionanocomposites in the medical and industrial field and as alternative resources of wood materials.