Study on the Friction and Wear Properties of Multiple Rare-Earth-Oxide-Reinforced Resin-Based Friction Materials.

Aiming to solve the problem of thermal decay of resin-based friction materials at high temperatures, rare-earth-lanthanum-oxide-/cerium-oxide-reinforced resin-based friction plates were prepared using a hot-pressing molding process. The effect of lanthanum/cerium oxide with different contents on the mechanical and tribological properties of the resin-based friction of materials was studied, and its mechanism was explored. The result shows that lanthanum/cerium oxide improves the mechanical and tribological properties of materials so that the coefficient of friction of the specimen is more stable on adding lanthanum/cerium oxide at 5% and 1%. Lanthanum/cerium oxide improves antidegradation properties of resin-based material and reduces the high-temperature wear rate by enhancing the interfacial effect so that the wear form of the specimen changes from predominantly adhesive wear to predominantly abrasive wear.