Nanocomposite hyaluronic acid adhesive hydrogel with controllable drug release for bone regeneration.

Hyaluronic acid (HA) hydrogels have arisen as candidate materials to simulate the extracellular matrix and restore the functions of both cartilage and hard bones. However, integration of bone tissue adhesion and long-term osteogenic properties in one hydrogel is often ignored. Herein, a strategy to construct nanocomposite hydrogel with host tissue adhesive properties, enhanced mechanical strength, improved stability and osteogenic effects was developed. Simvastatin (SIM) was firstly incorporated into zeolitic imidazolate framework-8 (ZIF-8) and surface decoration with hydroxyapatite was realized to obtain SIM loaded and hydroxyapatite modified ZIF-8 particles (SP). As the inorganic strengthening component, SP could further cross-link the mixture of dopamine-hyaluronic acid (dHA) and tannic (TA) via coordination interaction to fabricate the hybrid adhesive hydrogel (dHA/TA/SP). Sufficient phenolic groups endowed dHA/TA/SP with excellent tissue adhesion and antibacterial properties, while incorporation of SP significantly improved the mechanical strength and stability of hydrogel. Further, due to the multiple protective effects of ZIF-8 and hydrogel, SIM was sustainably released from dHA/TA/SP. Together with the active Zn and Ca, the expressions of ALP, OCN and RUNX2 were upregulated, and the mineralization was also promoted. With significant osteogenic effect in vitro and in vivo, this nanocomposite adhesive hydrogel holds great potential for bone defects repair.