The promotion of vascular reconstruction by hierarchical structures in biodegradable small-diameter vascular scaffolds.

Tissue engineering of small-diameter vessels remains challenging due to the inadequate ability to promote endothelialization and infiltration of smooth muscle cells (SMCs). Ideal vascular graft is expected to provide the ability to support endothelial monolayer formation and SMCs infiltration. To achieve this, vascular scaffolds with both orientation and dimension hierarchies were prepared, including hierarchically random vascular scaffold (RVS) and aligned vascular scaffold (AVS), by utilizing degradable poly(ε-caprolactone)-co-poly(ethylene glycol) (PCE) and the blend of PCE/gelatin (PCEG) as raw materials. In addition to the orientation hierarchy, dimension hierarchy with small pores in the inner layer and large pores in the outer layer was also constructed in both RVS and AVS to further investigate the promotion of vascular reconstruction by hierarchical structures in vascular scaffolds. The results show that the AVS with an orientation hierarchy that consists with the natural vascular structure had better mechanical properties and promotion effect on the proliferation of vascular cells than RVS, and also exhibited excellent contact guidance effects on cells. While the dimension hierarchy in both RVS and AVS was favorable to the rapid infiltration of SMCs in a short culture time in vitro. Besides, the results of subcutaneous implantation further demonstrate that AVS achieved a fully infiltrated outer layer with wavy elastic fibers-mimic strips formation by day 14, ascribing to hierarchies of aligned orientation and porous dimension. The results further indicate that the scaffolds with both orientation and dimension hierarchical structures have great potential in the application of promoting the vascular reconstruction.