Objectives: The purpose of this study was evaluating the performance of new Bis-EFMA based bulk-fill composites with common methacrylate based composites and commercial dental composites.
Methods: The Bis-EFMA monomer was synthesized and the novel Bis-EFMA based bulk-fill composites were prepared. The resin composite samples were co-cultured with human gingival epithelial cells and human dental pulp stem cells to test the biocompatibility. The edge adaptation was observed under a combination of stereoscope and scanning electron microscope. The internal hardness was measured using a Vickers microhardness tester after one-time filling of cavities prepared in extracted teeth. After friction and wear test on the surface of the resin composites, the surface morphology and volume wear of each group were measured by the optical profilometer. The color stability was measured by a colorimeter.
Results: Direct contact with human gingival epithelial cells and human dental pulp stem cells did not cause significant changes in their growth density and morphology, indicating good biocompatibility of Bis-EFMA group (p > 0.05). The continuous margin proportion of the Bis-EFMA group was as good as commercial bulk-fill composites (p > 0.05). The sectional microhardness results showed that the Bis-EFMA group had the highest microhardness. After the friction and wear test, the volume wear of the Bis-EFMA group was minimal, indicating its good wear resistance and mechanical strength. Color changes in all resin groups after 28 days of immersion were within the clinically acceptable range.
Significance: The addition of Bis-EFMA demonstrated excellent biocompatibility, edge adaptation and color stability comparable to commonly used clinical bulk-fill composites, along with preferable mechanical strength, friction and wear resistance. Bis-EFMA based bulk-fill composites have the potential to be employed as a bulk filling material in commercial dental composite applications.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1016/j.dental.2024.06.025 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Comparative Analysis of Conversion and Crosslinking Degree in Bulk-Fill, Monochromatic, and ORMOCER composites.
J Dent
January 2025
University of Saskatchewan, College of Dentistry. 107 Wiggins Rd, Saskatoon, SK, Canada. S7N 5E5. Electronic address:
Bulk-fill, monochromatic, and ORMOCER composites were introduced in restorative dentistry with the aim of reducing clinical time and/or alleviating contraction stresses at the interface between the tooth and restoration. While the conversion and immediate properties of these materials are comparable to conventional composites, studies evaluating their long-term properties and the structure of the polymer matrix are lacking. The objective of this study was to evaluate the degree of conversion and, indirectly, the crosslink density of conventional, bulk-fill, monochromatic, and ORMOCER resin composites.
View Article and Find Full Text PDFSurface roughness of composite resins subjected to brushing with whitening toothpastes: an in vitro study.
Braz Oral Res
January 2025
Pontifícia Universidade Católica do Rio Grande do Sul - PUC-RS, School of Health and Life Sciences, Department of Pediatric Dentistry, Porto Alegre, RS, Brazil.
The emergence of toothpastes containing different abrasive and whitening substances has been a constant concern among dental professionals. The aim of the present study was to perform an in vitro assessment of the surface topography of nanoparticle composite resins subjected to simulated brushing with dentifrices. Test samples were prepared with Filtek Universal (3M ESPE), Filtek Bulkfill (3M ESPE) and Z350 (3M ESPE), with 24 samples per resin.
View Article and Find Full Text PDFInfluence of the Type of Bulk-Fill, Resin-Based Composite on Internal Adaptation in Class V Restorations.
J Coll Physicians Surg Pak
January 2025
Department of Stomatology, The Second People's Hospital of Hefei and Hefei Hospital Affiliated to Anhui Medical University, Hefei, Anhui, China.
Objective: To investigate the effects of bulk-fill, resin-based composite types (high or low viscosity) on the internal adaptation of Class V restorations.
Study Design: Experimental study. Place and Duration of the Study: Hefei Stomatological Hospital, Hefei, China, from October 2022 to December 2023.
Resin composite aggregated S-PRG particles are not superior to non-S-PRG under microcosm biofilm.
Sci Rep
January 2025
Institute of Biology (Inbio), Universidade Federal de Mato Grosso do Sul, Campo Grande, MS, Brazil.
This study assessed the effect of composite resins, aggregated or not with S-PRG particles, and the use of toothpaste in controlling demineralization and bacterial growth. Human molars were distributed into 3 groups: control (CT) - sound teeth, Beautifil Bulk Restorative System (aggregated with S-PRG) (BB), Filtek One Bulk Fill (without S-PRG) (FB). Teeth destined for groups BB and FB previously received Class I preparations (4 × 4 × 4 mm), followed by single-increment restorations.
View Article and Find Full Text PDFExperimental study of polishing systems on surface roughness and color stability of novel bulk-fill composite resins.
BMC Oral Health
January 2025
Department of Endodontics, Faculty of Dentistry, Cukurova University, Adana, 01380, Turkey.
Objective: This in vitro study aimed to investigate the effect of five polishing systems on the surface roughness (SR) and color change (CC) of novel bulk-fill composite resins.
Methods: Fifty composite resin samples were prepared for each of the five groups: Stark Bulk Fill, SDR Plus, SonicFill 3, Charisma Bulk Flow One, and Filtek Z250. Each group of composite resins was further subdivided into five subgroups based on the polishing method applied: OptraGloss (OG), OptraGloss combined with Diapolisher paste (OG), OptiDisc (OD), OptiDisc combined with Diapolisher paste (OD), and Occlubrush (OCC) (n = 10).
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!