The surface of polytetrafluoroethylene (PTFE) bulk materials was modified by irradiation at high temperatures using a 1.2 MeV electron beam. The mass wear rate was decreased from 2.5 × 10 g N m to 0.08 × 10 g N m, and the hardness was increased from 33.2 MPa to 93.9 MPa. The yield strength was increased from 12.1 MPa to 25.8 MPa and Young's modulus was enhanced from 101 MPa to 261 MPa. The use of electron beam irradiation on PTFE at high temperature is an effective modification method to significantly improve its wear resistance and hardness, and increase the elastic response range of PTFE. The chemical reaction induced by electron irradiation at high temperature changes the molecular structure of the PTFE bulk material from highly linear to a network, thus improving the surface mechanical properties of PTFE.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1039/d4sm00359d | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Defining the Optimal Dose for 3-Dimensional Conformal Accelerated Partial Breast Irradiation: 15-Year Follow-Up of a Dose-Escalation Trial.
Int J Radiat Oncol Biol Phys
January 2025
Department of Radiation Oncology, Beth Israel Deaconess Medical Center, Harvard Medical School, Boston, Massachusetts.
Purpose: Randomized trials have demonstrated similar local tumor control in patients treated with accelerated partial-breast irradiation (APBI) compared with whole-breast irradiation. However, the optimal APBI dose for maximizing tumor control and minimizing toxicity is uncertain.
Methods And Materials: We enrolled patients ≥18 years of age with grade 1 or 2 ductal carcinoma in situ or stage I invasive breast cancer and resection margins ≥2 mm between 2003 and 2011 to a sequential dose-escalation trial using 3-dimensional conformal external beam APBI giving twice daily 4 Gy fractions with total doses of 32 Gy, 36 Gy, and 40 Gy.
Multifunctional Organic Molecule for Defect Passivation of Perovskite for High-Performance Indoor Solar Cells.
Materials (Basel)
January 2025
Key Laboratory of Applied Surface and Colloid Chemistry, National Ministry of Education, Shaanxi Key Laboratory for Advanced Energy Devices, Shaanxi Engineering Laboratory for Advanced Energy Technology, School of Materials Science and Engineering, Shaanxi Normal University, Xi'an 710119, China.
Perovskite solar cells (PSCs) can utilize the residual photons from indoor light and continuously supplement the energy supply for low-power electron devices, thereby showing the great potential for sustainable energy ecosystems. However, the solution-processed perovskites suffer from serious defect stacking within crystal lattices, compromising the low-light efficiency and operational stability. In this study, we designed a multifunctional organometallic salt named sodium sulfanilate (4-ABS), containing both electron-donating amine and sulfonic acid groups to effectively passivate the positively-charged defects, like under-coordinated Pb ions and iodine vacancies.
View Article and Find Full Text PDFRadiation Damage Mitigation in FeCrAl Alloy at Sub-Recrystallization Temperatures.
Materials (Basel)
December 2024
Department of Mechanical Engineering, The Pennsylvania State University, University Park, PA 16803, USA.
Traditional defect recovery methods rely on high-temperature annealing, often exceeding 750 °C for FeCrAl. In this study, we introduce electron wind force (EWF)-assisted annealing as an alternative approach to mitigate irradiation-induced defects at significantly lower temperatures. FeCrAl samples irradiated with 5 MeV Zr ions at a dose of 10 cm were annealed using EWF at 250 °C for 60 s.
View Article and Find Full Text PDFImproving Corrosion Resistance of Zircaloy-4 via High-Current Pulsed Electron Beam Surface Irradiation.
Materials (Basel)
December 2024
Ministry of Education Key Laboratory for Cross-Scale Micro and Nano Manufacturing, College of Mechanical and Electrical Engineering, Changchun University of Science and Technology, Changchun 130022, China.
Zircaloy-4 is extensively used in nuclear reactors as fuel element cladding and core structural material. However, the safety concerns post-Fukushima underscore the need for further enhancing its high-temperature and high-pressure water-side corrosion resistance. Therefore, this study aimed to investigate the effects of high-current pulsed electron beam (HCPEB) irradiation on the microstructures and corrosion resistance of Zircaloy-4, with the goal of improving its performance in nuclear applications.
View Article and Find Full Text PDFReview of the Synthesis and Degradation Mechanisms of Some Biodegradable Polymers in Natural Environments.
Polymers (Basel)
December 2024
Fujian Special Equipment Inspection and Research Institute, Fuzhou 350008, China.
The escalating demand for sustainable materials has been fueling the rapid proliferation of the biopolymer market. Biodegradable polymers within natural habitats predominantly undergo degradation mediated by microorganisms. These microorganisms secrete enzymes that cleave long-chain polymers into smaller fragments for metabolic assimilation.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!