Characterization and Implementation of Cocoa Pod Husk as a Reinforcing Agent to Obtain Thermoplastic Starches and Bio-Based Composite Materials.

When the cocoa pod husk (CPH) is used and processed, two types of flour were obtained and can be differentiated by particle size, fine flour (FFCH), and coarse flour (CFCH) and can be used as a possible reinforcement for the development of bio-based composite materials. Each flour was obtained from chopping, drying by forced convection, milling by blades, and sieving using the 100 mesh/bottom according to the Tyler series. Their physicochemical, thermal, and structural characterization made it possible to identify the lower presence of lignin and higher proportions of cellulose and pectin in FFCH. Based on the properties identified in FFCH, it was included in the processing of thermoplastic starch (TPS) from the plantain pulp () and its respective bio-based composite material using plantain peel short fiber (PPSF) as a reinforcing agent using the following sequence of processing techniques: extrusion, internal mixing, and compression molding. The influence of FFCH contributed to the increase in ultimate tensile strength (7.59 MPa) and higher matrix-reinforcement interaction when obtaining the freshly processed composite material (day 0) when compared to the bio-based composite material with higher FCP content (30%) in the absence of FFCH. As for the disadvantages of FFCH, reduced thermal stability (323.57 to 300.47 °C) and losses in ultimate tensile strength (0.73 MPa) and modulus of elasticity (142.53 to 26.17 MPa) during storage progress were identified. In the case of TPS, the strengthening action of FFCH was not evident. Finally, the use of CFCH was not considered for the elaboration of the bio-based composite material because it reached a higher lignin content than FFCH, which was expected to decrease its affinity with the TPS matrix, resulting in lower mechanical properties in the material.