Ultranarrow Deep-Blue Luminescence of Perovskite Nanocrystals by A-Site Cation Control.

Metal-halide perovskite nanocrystals (NCs) are one of the most promising emitters for the application of display and nanolight sources. The full width at half-maximum (FWHM) of photoluminescence (PL) emission is essential for color purity, which however remains a difficulty to further reduce the FWHM of the perovskite NCs at room temperature. Here, we show the quasi-sphere perovskite NCs with narrow PL emission at a deep-blue wavelength of ∼430 nm; its PL FWHM reaches ∼11 nm at room temperature, owing to the monodispersion in size distribution as well as the symmetric quasi-sphere morphology of NCs releasing the fine structure splitting-induced inhomogeneous broadening. Through regulating A cations with respect to the ratio of FA (or MA)-to-Cs and Cs-to-Pb, the PL emission of the NCs could be tuned from ∼505 to ∼430 nm combined with varied morphologies from large cube to small quasi-sphere. Such spectroscopic and morphological discrepancies are supposed to be attributed to the different crystalline kinetics that is strongly dependent on the synthetic condition. To be specific, in the case of increasing FA (or MA)-to-Cs, the growth rate of CsPbBr and FAPbBr (or MAPbBr) perovskites is determined by the reactivity of transient species, while in the case of decreasing the Cs-to-Pb ratio, the growth rate of perovskites is slowed down by the serious reduction of Cs in the precursor. This study provides an effective strategy to adjust the emission across from green to deep-blue color and promotes the perovskite NCs with a narrow FWHM, and tunable PL emission facilitates in application of optoelectronic devices.