Nano-architectonics of Pt single-atoms and differently-sized nanoparticles supported by manganese-oxide nanosheets and impact on catalytic and anti-biofilm activities.

Hybrid-nanozymes are promising in various applications, but comprehensive comparison of hybrid-nanozymes composed of single-atoms or nanoparticles on the same support has never been made. Here, manganese-oxide nanosheets were loaded with Pt-single-atoms or differently-sized nanoparticles and their oxidase- and-peroxidase activities compared. High-resolution Transmission-Electron-Microscopy and corresponding Fast Fourier Transform imaging showed that Pt-nanoparticles (1.5 nm diameter) had no clear (111) crystal-planes, while larger nanoparticles had clear (111) crystal-planes. X-ray Photo-electron Spectroscopy demonstrated that unloaded nanosheets were composed of MnO with a high number of oxygen vacancies (V/Mn 0.4). Loading with 7.0 nm Pt-nanoparticles induced a change to MnO, while loading with 1.5 nm nanoparticles increased the number of vacancies (V/Mn 1.2). Nanosheets loaded with 3.0 nm Pt-nanoparticles possessed similarly high catalytic activities as Pt-single-atoms. However, loading with 1.5 nm or 7.0 nm Pt-nanoparticles yielded lower catalytic activities. A model is proposed explaining the low catalytic activity of under- and over-sized Pt-nanoparticles as compared with intermediately-sized (3.0 nm) Pt-nanoparticles and single-atoms. Herewith, catalytic activities of hybrid-nanozymes composed of single-atoms and intermediately-sized nanoparticles are put a par, as confirmed here with respect to bacterial biofilm eradication. This conclusion facilitates a balanced choice between using Pt-single-atoms or nanoparticles in further development and application of hybrid-nanozymes.