Facile Fabrication of Highly Efficient Chitosan-Based Multifunctional Coating for Cotton Fabrics with Excellent Flame-Retardant and Antibacterial Properties.

Interest in the development of eco-friendly, sustainable, and convenient bio-based coatings to enhance flame retardancy and antibacterial properties in cotton fabrics is growing. In this work, chitosan was protonated at its amino groups using a method with a high atom economy using an equimolar amount of amino trimethylene phosphonic acid (ATMP), resulting in the fabrication of a single-component chitosan-based multifunctional coating (ATMP-CS), thereby avoiding any additional neutralization or purification steps. Cotton fabrics coated with various loads of ATMP-CS were prepared through a padding-drying-curing process. The morphology, thermal stability, mechanical properties, antibacterial properties, flame-retardant behavior, and flame-retardant mechanism of these fabrics were investigated. The coating exhibited excellent film-forming properties, and it imparted a uniform protective layer onto the surfaces of the cotton fabrics. When the load capacity reached 11.5%, the coated fabrics achieved a limiting oxygen index of 29.7% and successfully passed the VFT test. Moreover, the ATMP-CS coating demonstrated antibacterial rates against and reaching 95.1% and 99.9%, respectively. This work presents a straightforward and gentle approach to fabricating colorless, environmentally friendly, and highly efficient fabric coatings that have potential applications in promoting the use of bio-based materials.