Preparation of tomato peel pomace powder/polylactic acid foams under supercritical CO conditions: Improvements in cell structure and foaming behavior.

Polylactic acid (PLA) is an eco-friendly material that can help address the problems of petroleum depletion and pollution. Blending renewable biomass materials with PLA to create composite foams with a tunable pore structure, superior performance, and low cost is a green technique for improving the pore structure and mechanical characteristics of single PLA foams. PLA/TP composites were created using melted tomato peel pomace powder (TP), which has a lamellar structure, as a reinforcing agent. Then, the relationship between the vesicle structure, morphology, and properties of the PLA/TP composite foams produced through supercritical CO intermittent foaming were investigated. The findings revealed that TP considerably enhanced the rheological characteristics and crystalline behavior of PLA. The PLA/TP composite foam had a better cell structure, compression characteristics, and wettability than pure PLA. The expansion ratio of the PLA/TP composite could reach 18.8, and its thermal conductivity decreased from 174.2 mW/m·K at 100 °C to 57.8 mW/m·K at 120 °C. Furthermore, annealing before foaming decreased the average composite foam blister size from 110.09 to 66.53 μm, and the annealing process also improved compression performance. This study contributes to solving environmental difficulties and creating PLA foams with controlled bubble structures, uniform bubble sizes, and outstanding overall performance.