Preparation of a Polymeric Phosphoramide Flame-Retardant and Its Effect on the Flame-Retardant Properties of Epoxy Resin.

The flammability of epoxy resins and knowing how to achieve curing are particularly important factors during use. A novel approach for enhancing the fire resistance and reducing the smoke emission of epoxy resin during the curing process is suggested, which involves the utilization of a three-source integrated polymerization intumescent flame-retardant. In this study, the synthesis of poly 4,4-diaminodiphenylsulfone spirocyclic pentaerythritol bisphosphonate (PCS) is achieved through using solution polymerization, utilizing 4,4'-diaminodiphenylsulfone (DDS) and spirocyclic pentaerythritol bisphosphorate disphosphoryl chloride (SPDPC) as initial components. Following that, the EP underwent the inclusion of PCS to examine its resistance to heat, its ability to prevent flames, its effectiveness in reducing smoke and its curing effect. Compared to the unmodified epoxy resin, the addition of PCS can not only cure the epoxy resin, but also decompose before the epoxy resin and has a good carbonization effect. With the addition of 7 wt.% PCS, the LOI value can achieve 31.2% and successfully pass the UL-94 test with a V-0 rating. Moreover, the cone calorimeter experiment demonstrated a noteworthy decline of 59.7% in the maximum heat release rate (pHRR), 63.7% in overall heat release (THR), and 42.3% in total smoke generation (TSP). Based on the examination of TG-FTIR and SEM findings, there is ample evidence to suggest that PCS, functioning as a phosphorus-nitrogen intumescent flame-retardant that combines three origins, has the potential to exhibit a favorable flame-retardant impact in both its gas and condensed phases.