A Comparative Evaluation of Surface Properties of Cention N and TiO2-Enriched Cention N After Brushing Simulation and Erosive Challenge: An In Vitro Study.

Background This study aimed to evaluate and compare the abrasive and erosive wear resistance of Cention N and titanium dioxide (TiO) nanoparticle-enriched Cention N after three years of brushing simulation. Methodology A total of 48 freshly extracted mandibular molars were mounted in acrylic blocks and divided into two groups of 24 molars based on the type of restorative material used to restore them. Cavities of a standardized size were prepared. Group A was restored with Cention N, and group B was restored with 5% TiO-enriched Cention N. Each group was further divided into three subgroups of eight. Subgroup 1 was the control subgroup. Subgroup 2 was the abrasive subgroup, subjected to the abrasive challenge in a brushing stimulator with 30,000 cycles to 10,000 cycles in the linear X-axis and Y-axis each and another 10,000 cycles divided into 5,000 cycles clockwise and 5,000 cycles anticlockwise. The total number of brushing cycles was equal to three years of brushing with a duration of eight to nine hours. Subgroup 3 was the erosive and abrasive subgroup, subjected to an erosive pH cycle consisting of exposure to Coca‑Cola for five minutes thrice a day for seven days, and then subjected to brushing simulation as above. After the surface treatment, specimens were subjected to the Vickers microhardness test using a diamond indenter and the surface roughness test using an optical profilometer. The resulting values were subjected to statistical analysis. Results There was a significant decrease in mean surface roughness in group B, where TiO nanoparticles were added after erosive challenge and brushing simulation, than in group A. There was an increase in mean microhardness in group B which was not significant. Conclusions With the addition of 5% TiO to Cention N, there was a significant reduction in surface roughness. The surface microhardness of Cention N containing 5% TiO increased non-significantly compared to the control group.