New plant polyphenol-derived tannic acid-based chromium-free tanning agent for sustainable and clean leather production.

This study aimed to prepare a new bio-based chromium-free tanning agent. The green epoxide monocase ethylene glycol diglycidyl ether (EGDE) was grafted with tannic acid (TA) derived from natural plant using the one-pot method to synthesize new plant polyphenol-derived tannic acid-based chromium-free tanning agents (TA-EGDE) with abundant terminal epoxides. FTIR, H NMR, XPS, GPC, SEM, and other analytical techniques were used to characterize tanning agents. These consequences manifested that EGDE was successfully grafted with the phenol hydroxyl group of TA. The epoxide value of TA-EGDE showed a tendency to increase and then decrease with increasing EGDE dosage, and the epoxide value of TA-EGDE-2 attained a maximum of 0.262 mol/100 g. GPC analysis showed that the formula weight of the prepared TA-EGDE was partially distributed above 5000 Da. The tanning experiment demonstrated that the shrinkage temperatures (Ts) of the TA-EGDE-tanned leathers were all higher than 81.5 °C. Compared with the traditional commercial chromium-free tanning agent (F-90, TWS), TA-EGDE-tanned leathers exhibited higher Ts and better mechanical properties. The TA-EGDE prepared in this study not only has ecological environmental protection but also provides finished leather with good moisture, heat resistance, and mechanical properties.