Effect of canal medicaments triple antibiotic paste, Bio-C Temp, and Nano-silver gel activated by visible blue light on canal dentin microhardness and extrusion bond strength of AH plus sealer: A SEM and EDX analysis.

Aim: Assessment of contemporary canal medicaments (Triple antibiotic paste (TAP), Bio-C Temp, and Nano silver gel activated by visible blue light on the dentin microhardness (MH) and push-out bond strength (PBS) of AH plus endodontic sealer.

Method: Sixty extracted premolars were obtained and decontaminated. Canal cleaning and shaping were performed. The samples were randomly allocated into four groups based on the intracanal medicaments. Group 1= CH paste, Group 2= TAP, Group 3= Bio-C Temp, and Group 4= Nano-silver gel activated by visible blue light. MH assessment was performed using a Vickers Microhardness tester. Forty specimens, ten from each group underwent root canal obturation. PBS and failure mode evaluation were performed. ANOVA and Post Hoc Tukey test were utilized to conduct intra and inter-group comparisons.

Results: The maximum outcome of surface hardness was presented by Group-3 (Bio-C Temp®) specimens. However, minimum scores of MH were displayed by Group 1 (CH) treated teeth. The highest outcomes of EBS were exhibited by the cervical third of Group 3 (Bio-C Temp®) samples. The apical section of Group 4 Teeth with Nano Silver gel activated by visible blue light revealed the lowest scores of bond integrity.

Conclusion: Bio-C Temp and TAP proved to be better intracanal medicament than other tested groups in terms of the push-out bond strength of the sealer. TAP displayed lower microhardness as compared to the Bio-C Temp.