Parameters optimization for decontamination and fine physical regeneration pathways of polypropylene plastics from waste lunchboxes.

Due to the development of the food delivery industry, a large amount of waste lunchboxes made of homo polypropylene (PP) plastic have been generated. This study developed a new technological strategy to effectively regenerate PP from waste lunchboxes. Through response surface curve analysis, it was found that under the optimal process conditions of hot alkali washing at 80 ℃, 30 min, and pH 13, the optimal contact angle was 65.55°, indicating a good oil stain removal effect. By identifying and analyzing the characteristics of impurities in waste lunchboxes, a physical sorting and granulation regeneration process was constructed. And through large-scale statistical analysis and data collection, it was further verified that recycled PP plastics maintained their physical stability and excellent processing performance. The quality stability of recycled PP plastics in terms of impurities content was also verified. By designing different formulations specifically, recycled PP was mixed with different virgin PP and antioxidants in appropriate proportions, and extruded into particles under 150-300 mesh filtration conditions to obtain modified recycled PP. Modified recycled PP was applied in textiles, clothing, and injection molded products. In conclusion, we achieve the up-cylcing of waste PP lunchboxes instead of down-cylcing.