Effect of Casein Phosphopeptide-Amorphous Calcium Phosphate, Proanthocyanidin, Carbon Dioxide Laser Remineralization on the Bond Integrity of Composite Restoration Bonded to Caries-Affected Dentin.

Assessment of different remineralizing pretreatment casein phosphopeptide-amorphous calcium phosphate (CPP-ACP), proanthocyanidin (PA), carbon dioxide laser (CO), eggshell solution (ES) on the shear bond strength (SBS) of resin composite bonded to remineralized carious-affected dentin (CAD). Eighty human molars were collected with occlusal caries that extended about halfway into the dentin. Using a water-cooled, low-speed cutting saw, a flat, mid-coronal dentin surface was exposed. CAD was differentiated from healthy dentin. Based on the remineralizing agent used on the CAD surface, the teeth were arbitrarily allocated into five groups ( = 10). Group 1: no remineralizing agent, Group 2: CPP-ACP, Group 3: 6.5% PA solution, Group 4: CO laser, and Group 5: ES solution. All samples were bonded to composite and light cured and thermocycled. SBS and failure mode analysis were performed using universal testing and stereomicroscope 40 × . Using SPSS, SBS, and failure mode data were analyzed using analysis of variance and Tukey's honesty significant difference (HSD) test Group 3 (6.5% PA solution; 15.59 ± 1.44 MPa) samples established the maximum bond integrity. Nevertheless, Group 1 (No remineralizing agent; 11.19 ± 1.21 MPa) exhibited the minimum outcome of bond strength. Intergroup comparison analysis showed that Group 1 (No remineralizing agent), Group 2 (CPP-ACP), and Group 4 (CO laser) established comparable values of bond strength ( > 0.05). Likewise, Group 3 (6.5% PA solution) and Group 5 (EA solution) also revealed equivalent bond integrity ( > 0.05). PA and ES are considered potential remineralizing agents used for caries-affected dentin surfaces in improving bond integrity to composite resin. However, further studies are advocated to extrapolate the findings of this study.