Hyaluronic acid hydrogels with excellent self-healing capacity and photo-enhanced mechanical properties for wound healing.

A continuously stable moist healing environment is immensely beneficial for wound healing, which can be availably achieved by providing an in situ hydrogel with enough strength resembling skin tissue and self-healing ability. Herein, through a dual-crosslinking strategy, hyaluronic acid-based hydrogels with excellent self-healing capacity and enhanced mechanical properties are fabricated via the acylhydrazone linkages and subsequent photocrosslinking based on hydrazide-modified sodium hyaluronate and aldehyde-modified maleic sodium hyaluronate. The hydrogels demonstrate the fast gelation process (< 1 min), the controlled swelling behaviors, and the good biocompatibility. Notably, they possess enhanced mechanical strength similar to the human dermis (∼ 2.2 kPa). Also, they can self-heal rapidly with a self-healing efficiency of ∼90 % at 6 h. Based on this, the hyaluronic acid-based hydrogels, without any biological factors involved, can facilitate the full-thickness skin wound reconstruction process by accelerating the three phases of the wound repair, including reducing wound inflammation in the inflammatory phase, promoting angiogenesis in the proliferative phase, and promoting the deposition and reconstruction of collagen in the remodeling phase. The produced hyaluronic acid hydrogel can serve as an ideal candidate for wound healing.