Investigation of Layered Structure Formation in MgB Wires Produced by the Internal Mg Coating Process under Low and High Isostatic Pressures.

Currently, MgB wires made by the powder-in-tube (PIT) method are most often used in the construction and design of superconducting devices. In this work, we investigated the impact of heat treatment under both low and high isostatic pressures on the formation of a layered structure in PIT MgB wires manufactured using the Mg coating method. The microstructure, chemical composition, and density of the obtained superconductive wires were investigated using scanning electron microscopy (SEM) with an energy-dispersive X-ray spectroscopy (EDS) analyzer and optical microscopy with Kameram CMOS software (version 2.11.5.6). Transport measurements of critical parameters were made by using the Physical Property Measurement System (PPMS) for 100 mA and 19 Hz in a perpendicular magnetic field. We observed that the Mg coating method can significantly reduce the reactions of B with the Fe sheath. Moreover, the shape, uniformity, and continuity of the layered structure (cracks, gaps) depend on the homogeneity of the B layer before the synthesis reaction. Additionally, the formation of a layered structure depends on the annealing temperature (for Mg in the liquid or solid-state), isostatic pressure, type of boron, and density of layer B before the synthesis reaction.