Tin-based perovskite solar cells (TPSCs) have received increasing attention due to their low toxicity, high theoretical efficiency, and potential applications as wearable devices. However, the inherent fast and uncontrollable crystallization process of tin-based perovskites results in high defect density in the film. Meanwhile, when fabricated into flexible devices, the prepared perovskite film exhibits inevitable brittleness and high Young's modulus, seriously weakening the mechanical stability. In this work, we design and synthesize a cross-linkable fullerene, thioctic acid functionalized C fulleropyrrolidinium iodide (FTAI), which has multiple interactions with perovskite components and can finely regulate the crystallization quality of perovskite film. The obtained perovskite film shows an increased grain size and a more matched energy level with the electron transport material, effectively improving the carrier extraction efficiency. The FTAI-based rigid device achieves a champion efficiency of 14.91 % with enhanced stability. More importantly, the FTAI located at the perovskite grain boundaries could spontaneously cross-link during the perovskite annealing process, which effectively improves the conductivity and elasticity of grain boundaries, thereby giving the film excellent bending resistance. Finally, the FTAI-based wearable device yields a record efficiency of 12.35 % and displays robust bending durability, retaining about 90 % of the initial efficiency after 10,000 bending times.
Download full-text PDF |
Source |
---|---|
http://dx.doi.org/10.1002/anie.202402775 | DOI Listing |
J Phys Chem B
December 2024
Department of Physics, University of South Florida, Tampa, Florida 33620, United States.
Using a Lubachevsky-Stillinger-like growth algorithm combined with biased SWAP Monte Carlo and transient degrees of freedom, we generate ultradense disordered jammed ellipse packings. For all aspect ratios α, these packings exhibit significantly smaller intermediate-wavelength density fluctuations and greater local nematic order than their less-dense counterparts. The densest packings are disordered despite having packing fractions ϕ(α) that are within less than 0.
View Article and Find Full Text PDFSci Rep
December 2024
Institute of Applied Physics, Jiangxi Academy of Sciences, Nanchang, 330096, China.
Cu-1.33Ni-1.35Sn-0.
View Article and Find Full Text PDFSmall
December 2024
Beijing Key Laboratory for Magneto-Photoelectrical Composite and Interface Science, School of Mathematics and Physics, University of Science and Technology Beijing, Beijing, 100083, P. R. China.
The study presents a multi-functional and semiconductor polymer poly[bis(3-hexylthiophen-2-yl)thieno[3,4-c]pyrrole-4,6-dione] (PBDTTPD) doping strategy that significantly enhanced the performance of the two-terminal all-perovskite tandem perovskite solar cells (T-PSCs). An optimized power conversion efficiency (PCE) of 26.87% has been achieved.
View Article and Find Full Text PDF3D Print Addit Manuf
December 2024
School of Optical and Electronic Information, Huazhong University of Science and Technology, Wuhan, P.R. China.
Thermal cracking is one of the serious issues that deteriorates the processibility of laser powder bed fusion (LPBF) high-strength aluminum components. To date, the effects of processing parameters on crack formation are still not well understood. The purpose of this study is to understand the correlation between the thermal cycle and the hot cracking during LPBF of Al-Cu-Mg-Mn alloys.
View Article and Find Full Text PDFMicron
December 2024
Department of Chemical and Materials Engineering, The University of Auckland, New Zealand. Electronic address:
This study investigates the effect of pre-deformation by cold rolling after solution annealing on the microstructure and properties of the fine-grained Al-Li alloy 2A97. Electron backscatter diffraction (EBSD), X-ray diffraction (XRD) and transmission electron microscopy (TEM) were used to characterize grain boundaries, dislocations, precipitates and calculate their contribution to strength. It is found that the changes in precipitation behavior predominantly account for the enhanced tensile properties observed in the deformed alloys, where yield and tensile strengths are increased by 85 MPa and 63 MPa, respectively.