A novel biodegradable magnesium skin staple: A safety and functional evaluation.

Background: The potential of biodegradable magnesium (Mg) skin staple has recently garnered widespread attention due to their biodegradability and biocompatibility rather than traditional stainless steel staples, the most commonly used in current clinical practice. The aim of this study is to evaluate the safety and mechanical properties of a novel biodegradable Mg skin staple.

Methods: A prototype of Mg skin staple was designed using a novel ZK60 Mg alloy. The mechanical properties of the staple were evaluated using a universal testing machine. The cytotoxicity of the staple was examined in vitro and the efficacy of the staple in wound closure was assessed in New Zealand rabbits for one and three weeks, respectively.

Results: The tensile strength of this Mg alloy is 258.4 MPa with 6.9% elongation. The treatment of HaCaT and L929 cells with the staple extract resulted in over 95% cell viability, indicating no cytotoxicity. In vivo, no tissue irritation was observed. No difference was found in wound healing between the Mg skin staple and the stainless steel staple after one and three weeks in the cutting wound on the back of rabbits. Some Mg skin staples spontaneously dislodged from the skin within three weeks, while others were easily removed.

Conclusion: Our results confirm the safety, biocompatibility, and functionality of the novel Mg skin staple in wound closure. The efficacy of the staple in wound closure was demonstrated to be as effectively as conventional staples, with the added benefit of decreased long-term retention of skin staples in the wounds.