KCO-Modified Smectites as Basic Catalysts for Glycerol Transcarbonation to Glycerol Carbonate.

A novel and cost-effective heterogeneous catalyst for glycerol carbonate production through transesterification was developed by impregnating smectite clay with KCO. Comprehensive structural and chemical analyses, including X-ray diffraction Analysis (XRD), Scanning Electron Microscopy (SEM)-Electron Dispersion Spectroscopy (EDS), Fourier Transform Infrared Spectroscopy (FTIR), and Brunauer-Emmett-Teller (BET) surface area analysis measurements, were employed to characterize the catalysts. Among the various catalysts prepared, the one impregnated with 40 wt% KCO on smectite and calcined at 550 °C exhibited the highest catalytic activity, primarily due to its superior basicity. To enhance the efficiency of the transesterification process, several reaction parameters were optimized, including the molar ratio between propylene carbonate and glycerol reactor loading of the catalyst and reaction temperature. The highest glycerol carbonate conversion rate, approximately 77.13% ± 1.2%, was achieved using the best catalyst under the following optimal conditions: 2 wt% reactor loading, 110 °C reaction temperature, 2:1 propylene carbonate to glycerol molar ratio, and 6h reaction duration. Furthermore, both the raw clay and the best calcined KCO-impregnated catalysts demonstrated remarkable stability, maintaining their high activity for up to four consecutive reaction cycles. Finally, a kinetic analysis was performed using kinetic data from several runs employing raw clay and the most active KCO-modified clay at different temperatures, observing that a simple reversible second-order potential kinetic model of the quasi-homogeneous type fits perfectly to such data in diverse temperature ranges.