In situ sono-rheometric assessment of procaine-loaded calcium pectinate hydrogel for enhanced drug releasing under ultrasound stimulation.

Ultrasound (US) triggered alterations in the viscoelastic behavior of the procaine-loaded ionically gelatinized pectin hydrogel matrix, and drug release was observed using a sono-device rheometer. The gel softened immediately upon activation of the ultrasound operated at 43 kHz and remained in a softened state throughout the irradiation. Upon cessation of ultrasound, the gel promptly reverted to its original hardness. This cycle of softening was consistently observed in ionically crosslinked pectin hydrogels, resulting in the promotion of procaine release, particularly with higher US power and lower calcium concentration. As the amount of loaded procaine increased, the gel weakened due to ion exchange with the calcium crosslinker and procaine. The most substantial release efficiency, reaching 82 % with a concentration of 32 μg/ml, was achieved when the hydrogels contained 0.03 % procaine within the gelatinized hydrogel medicine at a calcium concentration of 0.9 M, representing a six-fold increase compared to that without US. Notably, US exposure affected the 3D porous structure and degradation rate, leading to hydrogel collapse and facilitating medicine release. Additionally, the procaine-loaded pectin hydrogels with 0.9 M calcium exhibited improved fibroblast cell viability, indicating non-toxicity compared to those hydrogels prepared at a higher Ca concentration of 2.4 M.