Colossal Magnetoresistive Switching Induced by d Ferromagnetism of MgO in a Semiconductor Nanochannel Device with Ferromagnetic Fe/MgO Electrodes. | LitMetric
Department of Electrical Engineering and Information Systems, The University of Tokyo, 7-3-1 Hongo, Bunkyo-ku, Tokyo, 113-8656, Japan.
Published: June 2024
AI Article Synopsis
Article Abstract
Exploring potential spintronic functionalities in resistive switching (RS) devices is of great interest for creating new applications, such as multifunctional resistive random-access memory and novel neuromorphic computing devices. In particular, the importance of the spin-triplet state of cation vacancies in oxide materials, which is induced by localized and strong O-2p on-site Coulomb interactions, in RS devices has been overlooked. d ferromagnetism sometimes appears due to the spin-triplet state and ferromagnetic Zener's double exchange interactions between cation vacancies, which are occasionally strong enough to make nonmagnetic oxides ferromagnetic. Here, for the first time, anomalous and colossal magneto-RS (CMRS) with very high magnetic field dependence is demonstrated by utilizing an unconventional RS device composed of a Ge nanochannel with all-epitaxial single-crystalline Fe/MgO electrodes. The device shows colossal and unusual behavior as the threshold voltage and ON/OFF ratio strongly depend on a magnetic field, which is controllable with an applied voltage. This new phenomenon is attributed to the formation of d-ferromagnetic filaments by attractive Mg vacancies due to the spin-triplet states with ferromagnetic double exchange interactions and the ferromagnetic proximity effect of Fe on MgO. The findings will allow the development of energy-efficient CMRS devices with multifield susceptibility.
Exploring potential spintronic functionalities in resistive switching (RS) devices is of great interest for creating new applications, such as multifunctional resistive random-access memory and novel neuromorphic computing devices. In particular, the importance of the spin-triplet state of cation vacancies in oxide materials, which is induced by localized and strong O-2p on-site Coulomb interactions, in RS devices has been overlooked. d ferromagnetism sometimes appears due to the spin-triplet state and ferromagnetic Zener's double exchange interactions between cation vacancies, which are occasionally strong enough to make nonmagnetic oxides ferromagnetic.
The tunnelling electric current passing through a magnetic tunnel junction (MTJ) is strongly dependent on the relative orientation of magnetizations in ferromagnetic electrodes sandwiching an insulating barrier, rendering efficient readout of spintronics devices. Thus, tunnelling magnetoresistance (TMR) is considered to be proportional to spin polarization at the interface and, to date, has been studied primarily in ferromagnets. Here we report observation of TMR in an all-antiferromagnetic tunnel junction consisting of MnSn/MgO/MnSn (ref.
Ultrathin MgO(100) films serving as a diffusion barrier between ferromagnetic electrodes and GaAs(001) semiconductor templates have been investigated. Using Fe as an exemplary ferromagnetic material, heterostructures of Fe/MgO/GaAs(001) were prepared at 200 °C with the MgO thickness ranging from 1.5 to 3 nm.
The transport properties of magnetic tunnel junctions (MTJs) are very sensitive to interface modifications. In this work we investigate both experimentally and theoretically the effect of asymmetric barrier modifications on the bias dependence of tunneling magnetoresistance (TMR) in single crystal Fe/MgO-based MTJs with (i) one crystalline and one rough interface, and (ii) with a monolayer of O deposited at the crystalline interface. In both cases we observe an asymmetric bias dependence of TMR and a reversal of its sign at large bias.
State Key Laboratory of Magnetism, Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100190, China.
Following predictions by first-principles theory of a huge tunnel magnetoresistance (TMR) effect in epitaxial Fe/MgO/Fe magnetic tunnel junctions (MTJs), measured magnetoresistance (MR) ratios of about 200% at room temperature (RT) have been reported in MgO-based epitaxial MTJs. Recently, a MR ratio of about 600% has been reported at RT in MgO-based MTJs prepared by magnetron sputtering, using amorphous CoFeB as the ferromagnetic electrode. These MTJs show great potential for application in spintronic devices.